提高1.0619WCBLCC和1.6220钢热处理后的硬度即抗拉强度有利于提高低温冲击功.docVIP

提高1.0619、WCB、LCC和1.6220钢热处理后的硬度即抗拉强度 摘要：本文通过对中，美，德，日和俄罗斯标准中关于C、C-Mn压力容器用钢的抗拉强度（Rm）规定上限的比较，结合现场进行的大量随炉热处理试的统计分析，论述了德标1.0619（GP240GH）中规定了Rm上限（600Mpa），是不利于提高材料的性能和使用性能的，而且也降低了加工性能和不便热处理组织生产。中、日和俄标准中不设Rm上限，这有利于挖掘材料的潜力，提高材料的使用性能并节能。 关键词：抗拉强度（Rm）上限 Analyzing Upper Limit Rm of Steels (C, C-Mn) for Pressure Vessel in Several Countries MuZhe-yua (Luoyang Zhongnuo Machinery Manufacturing Co., Ltd 471822, China) Abstract：The author has performed and analyzed tremendous statistics of mechanical properties for test bar along with heat treating furnace. Compared with different standards of Rm (tensile strength) of steels (C, C-Mn) for pressure vessel in China, United States, Germany, Japan and Russia, German standard 1.0619(GP240GH) upper limit Rm is 600 Mpa that is the lowest standard. This upper limit Rm is not conductive to improve mechanical and material performance, reducing processing performance, and increasing inconveniences of Heat Treatment process. However, Chinese, Japanese, and Russian standards, without upper limit Rm, are easier to improve material and mechanical properties, and saving energy. When standards could not be changed, users could choose higher level standards. Key words: tensile strength（Rm）upper limit；Akv；1.0619；WCB；LCC；1.6220 1、几个国家Rm上限规定情况： 生产中常用的高温阀门用钢有WCB、WCC和1.0619，低温LCB、LCC、1.6220和20гл。WCB和LCB为C钢（碳钢），其它为C-Mn（碳锰）。不同国家指标不同，详见表1。高温Re 240～250Mpa和275～280Mpa为相同强度等级。低温LCC、1.6220和20глRe为275～300Mpa为相同强度等级。Rm不设上限的有中国高温用钢，还有日本和俄罗斯高、低温用钢。美WCB、WCC和LCC Rm上限为655Mpa，德标1.为60Mpa，1.0619的Rm上限最低 几个国家的C、C-Mn高、低温压力容器用钢要求 表1 国别 钢号 Rm(Mpa) Re≥(Mpa) A≥(%) Z≥(%) 试验温度℃ Akv≥(J) AVG≥(J) 热处理 备注 中国 2G240-450BG BD 450～600 240 22 35 室温 45 GB/T 16253-1996 -40 27 2G280-520BG BD 520～670 280 18 30 室温 35 GB/T 16253-1996 -40 27 2G205-415 WCA ≥415 205 24 35 GB/T 12229 -2005 2G250-485 WCB ≥485 250 35 2G275-485 WCC ≥485 275 22 35 LCB 450～620 240 24 35 -46 14 18 JB/T 7248 -2008 LCC 485～665 275 22 35