有机钛PC-500交联羟丙基瓜尔胶压裂液* 卿鹏程 　　摘要：用有机钛、胺基醇和乳酸合成了有机钛交联剂PC-500，研究了羟丙基瓜尔胶／有机钛PC-500水基冻胶压裂液的配方，得到了可耐温100℃以上，抗剪切，低残渣，交联时间可调的压裂液。在配方研究中特别考察了冻胶稳定剂、pH调节剂的作用。　　关键词：有机钛交联剂；羟丙基瓜尔胶／有机钛冻胶压裂液；配方研究　　中图分类号：TE39：TE357.1+2　　　文献标识码：A PREPARATION OF HYDROXYPROPYL GUAR GUM／TITANORGANICCROSSLINKER PC-500 AQUEOUS HYDROFRACTURING FLUID QIN Peng Cheng(Liaohe Petroleum Professional School,Panjing,Liaoning,124103,China) 　　Abstract：A titanoranic crosslinker,PC-500,is prepared from a titanorganic compound,an aminoalcohol,and malonic acid.With PC-500,a formulation of hydroxypropyl guar based aqueous hydrofracturing fluid is optimized on the basis of screening ingredients,particularly oxygen scavenger Na2S2O3 and pH adjasting agent fumanic acid +NaHCO3.The high viscosity (～90 mPa.s) of a formulated fluid maintains unchanging at least in 2 hrs at 100℃ and shear rate 170 1/s.With or without a gel breaker the gelled fluid breaks down at 100—150℃ in 24—30 hrs with small amount of solid residue left.The fluid is developed for high-temperature and low-permeability reservoirs.　　Key Words: Titanorganic Crosslinker; Hydroxypropyl Guar/Titanium Aqueous Gelling Hydrofracturing Fluid; Formulations 　　本文报道的有机钛交联羟丙基瓜尔胶压裂液，是一种适用于高温油藏的冻胶体系。增粘剂之所以选用羟丙基瓜尔胶，是由于它增粘能力强，水不溶物含量低，已在国内外获得广泛应用〔1—3〕。本文报道的钛冻胶由于使用了我们研制的交联剂PC-500，抗热剪切性能极好，在高温(100℃)、一般流经油管时的剪切速率(170 s-1)下至少在2小时内可以维持高粘度，因此可以满足携砂、造缝等压裂施工要求，且破胶后残渣量低，可望用于高温低渗透油藏。 　　1　压裂液配方研究 　　在以下配方研究中所用的实验压裂液由羟丙基瓜尔胶HPG(增粘剂)、PC-500(有机钛交联剂)、SP169(破乳剂)、氯化钾KCl(粘土稳定剂)、富马酸FA+碳酸氢钠NaHCO3(pH调节剂)、硫代亚硫酸钠Na2S2O3(冻胶稳定剂)、BE-4+TA-1227(杀菌剂)配制而成。在考察各组分用量的实验中，除作为变量的该组分外其余组分的用量均保持不变。　　1.1　羟丙基瓜尔胶用量　　所用羟丙基瓜尔胶为山东东营油田化学联营公司产品。压裂液的表观粘度用Fann-35型粘度计在100℃、170 s-1下测定。　　图1所示为羟丙基瓜尔胶用量为0.60%、0.65%、0.70%的实验压裂液在温度100℃、剪切速率170 s-1下连续剪切2小时过程中表观粘度的变化。羟丙基瓜尔胶用量为0.65%的压裂液抗热抗剪切性能最好，在这种热剪切条件下，冻胶形成后至少在2小时内粘度不下降。因此，压裂液中羟丙基瓜尔胶的用量选为0.65%。 图1　HPC浓度不同的HPG/PC-500实验压裂液的表现粘度与热剪切时间关系曲线 　　1.2　Na2S2O3用量　　Na2S2O3在压裂液中起冻胶稳定剂的作用，加入Na2S2O3是为了除去压裂液中的溶解氧。除氧化学反应为：　　　　Na2S2O3→Na2SO3+S　　　　2Na2SO3+O2→2Na2SO4　　Na2S2O3加量为0.05%、0.10%、