粉煤灰基复合胶剂在全尾砂充填中的应用.doc

粉煤灰基多元复合胶结剂在全尾砂充填中的应用 杨春保⒈ 朱春启⒈　陈贤树⒉ 1合肥水泥研究设计院；2 北京菲恩科技有限公司 摘 要：简述了粉煤灰基多元复合胶结剂的生产工艺过程，及其在矿山全尾砂胶结充填中的应用。实践表明，粉煤灰基多元复合胶结剂性能良好、生产成本低廉。完全替代水泥用于矿山全尾砂充填，可用超低的灰砂比、有更好的流动输送性能，更低的充填成本。 关键词：粉煤灰 胶结剂 全尾砂 充填成本 Application in Mine Whole Tail Sand Filling of Fly Ash Based Compound Cementation Material Yang Chunbao⑴ Zhu Chunqi ⑴ Cheng Xianshu⑵ ⑴Hefei Cement Research and Design Institute ⑵Bejing Keen Science and Technology Limited Company Abstract The produced technological process and the application in mine whole tail sand filling of fly ash based compound cementation material is described briefly. It is indicated that fly ash based compound cementation material has a nicer performance and a lower made cost than cement. It can replaces cement entirely to be used in mine whole tail sand filling with super low ash—sand ratio and better performance of flow and transport. Key words fly ash, cementation material, whole tail sand, filling cost 对矿山井下充填，国家环保政策从过去的“可选”提升到现在的“必须”。矿山全尾砂充填，过去都用水泥做胶结剂，近几年也有用高细粉磨矿渣代替水泥的，取得了较好的成效。 与矿渣相比，粉煤灰价格便宜，来源广泛，而且可以改善混凝土的流动性、和易性、抗渗性等性能，但早期水化活性激发难度大。对粉煤灰进行活性激发，国内外学者都作过大量的试验研究，取到了许多技术进展⑴，但这些技术大量应用于实际工业生产尚不多见。合肥水泥研究设计院受安徽金安矿业有限公司的委托，与北京菲恩科技有限公司合作，经过大量科学试验，研制出以粉煤灰为主要原料，外加脱硫石膏、石灰石渣、矿渣等工业废弃物和少量水泥熟料、专用激发剂生产的适宜于矿山井下全尾砂胶结充填的粉煤灰基复合胶结剂（以下简称粉煤灰基胶结剂），并在安徽金安矿业有限公司草楼铁矿设计、建设了一条年产100万吨的粉煤灰基胶结剂生产线。一期工程（年产30万吨）于2010年7月正式投产，所生产的产品已全部用于草楼铁矿及周边的铁矿井地下充填工程。经过近一年的生产应用，显现了良好的社会经济效益。 本文试对这一环保型高科技产品的生产应用作一简要综述。 1 粉煤灰基胶结剂的生产工艺过程 粉煤灰基胶结剂的生产原料为：粉煤灰、矿渣、水泥熟料、脱硫石膏、石灰石渣和专用激发剂等，其中粉煤灰占40%以上。矿渣和粉煤灰分别来自南京钢铁联合集团公司和埠阳、淮南火电厂，其它原料在当地就近采购。 生产工艺过程：湿矿渣由堆场经皮带秤计量入高效回转式烘干机，烘干后入干渣库储存备用。其它物料分别入库备用。根据物料的粒度及易磨性将生产原料分成两组：矿渣、水泥熟料、脱硫石膏、石灰石渣为一组，粉煤灰和激发剂为另一组，分别采用开流矿渣微粉管磨系统及开流粉煤灰微粉管磨系统，进行高细粉磨后入库。之后两组物料再经粉煤灰微粉转子秤计量，按一定比例配制，经混料机混合均匀成为粉煤灰基胶结剂。通过输送设备输送至成品库，再由气力输送设备送至充填站储库备用。主要设备高效烘干机湿矿渣由堆场经皮带秤计量入高效回转式烘干机，烘干后入干渣库储存备用。其它物料分别入库备用。根据物料的粒度及易磨性将生产原料分成两组：矿渣、水泥熟料、脱硫石膏、石灰石渣为一组；粉煤灰和激发剂为另一组，分别采用开流矿渣微粉管磨系统及开流粉煤灰微粉管磨系统，进行高细粉磨后入库。之后两组物料、粉煤灰