谈新型干法水泥生产中熟料的质量分析与控制zhx.docVIP

《水泥质量控制分析》 课程论文 浅谈新型干法水泥生产中熟料的质量分析与控制 姓名： 赵晗旭 班级：无机111 学号：119024286 2015/1/8 谈新型干法水泥生产中熟料的质量分析与控制 1、摘要 随着国民经济的持续增长，出现了一个以新型干法水泥为代表的高速增长的势头，引起国内外同行的关注。新型干法水泥生产由于采用了新工艺,新技术，使得水泥熟料单产能耗不断降低，生产效率不断提高，产品质量也不断提高，水泥生产运行与管理正向着高质量，集约化的方向发展。水泥生产质量控制的环节主要包括原燃材料和辅助材料的控制，生料的控制，熟料的控制，水泥的控制等几个方面，本文主要阐述新型干法水泥生产中熟料的质量分析与控制。 Abstract: With the continued growth of the national economy, there has been a tendency to dry cement as the representative of the rapid growth caused concern domestic and foreign counterparts. Cement production as a result of the adoption of new technology, new technology, making cement clinker yields continue to reduce energy consumption, and continuously improve productivity, product quality is also rising, cement production and operation and management direction is toward high-quality, intensive development . The?cement?production?aspects?of?quality?control?include?the?control?of?raw?materials?and?fuel?and?auxiliary?materials,?raw?material?control?,?control?of?clinker,?cement?control?,?and?several?other?aspects,?this?paper?describes?the?production?of?new?dry?process?cement?clinker?quality?analysis?and?control. 关键词：新型干法水泥 熟料 质量分析与控制 Key word ：cement;?clinker;?quality?analysis?and?control 根据水泥品种，原料的物理化学性能，与具体生产条件，确定所用原料配合比，以得到煅烧水泥熟料所需要适当成份的生料，称为生料的配料，简称配料。 合理的配料方案即是工艺设计的依据，又是正常生产的保证。配料包括原料的选择、熟料的设计与生料配料计算。 2、熟料组成的选择及注意的问题。 熟料的质量控制项目主要包括熟料的化学成分?(即KH,?n,?P)、熟料中游离CaO含量、熟料中MgO含量、熟料立升重、熟料烧失量、熟料物理性能?(凝结时间、安定性和强度)这几个方面。 合理的配料方案，表现在熟料矿物成份的选择上，即对三个率值的确定，为获得优质熟料，应以以下几方面考虑。 1、水泥品种：为满足不同品种水泥的要求，应选择不同矿物组成。如生产快硬硅酸盐水泥，需要较高的早期强度，则应提高熟料中C3S和C3A的含量，低热水泥（中抗水泥）则要求水化热低，抗硫酸盐侵蚀性能好。则相应提高C2S和C4AF含量。 2、原料的品种、生料易烧性：原料的化学成份与工艺性能，往往对熟料组成的选择有较大的影响。如石灰石燧石多，粘土含砂量多，则应适当降低KH来适应原料的实际情况。生料易烧性好，可以选择较高的KH、高SM的配料方案。反之，只能配低一些。 3、燃料质量：燃料品质对率值及煅烧影响较大，燃煤不单供给热量，煤灰还起配料作用，煤质差，灰份大，应相应降低熟料KH。 4、KH的选择：若工艺条件好，生料均化性好，或使用矿化剂，操作水平高，可适当提高KH，KH高则C3S含量增加，熟料强度高。综合考虑，要选择合适的KH。 5、SM的选择：SM选择应与KH相适宜，应避免以下倾向： （1）、KH高，SM也高，熔剂矿物少，吸收f-CaO反应不完全，熟料不易烧结，f-CaO高。 （2）、SM高，KH低，C2S高，易造成熟料粉化，熟料强度低。 （