第一次文献汇报概要.pptVIP

Literature Review name:xiang yuchun Anodic aluminum oxide nanograting for back light trapping in thin c-Si solar cells Introduction Simulation model Results and discussion Conclusions Contents 1.Introduction thin Si solar cells saved materials, low costs Photoelectric conversion efficiency is low Surface texturing, nanowires, using surface plasmon effect, producing a multilayer coupling structure is a common method for surface light trapping subwavelength grating with metal reflectors photonic crystals structures the influence of AAOs geometrical parameters and parameter tolerance on light trapping AAO nanograting and Ag thin layer 2.Simulation model Fig. 1. Simulation model: d is the thickness of AAO, a is the distance between the AAO holes and h is the height of Si active layer 3.Results and discussion Relationship between Jscand AAO parameters in simulation Fig. 2. Relationship between Jsc and AAO geometrical parameters: (a), (b), (c), and (d) is for the period of 100, 200, 300 and 400 nm respectively. 3.Results and discussion AAO parameter optimization based on simulation Fig. 3. Relationship between duty circle and Jscenhancement (here we set AAOs thickness as 78.6 nm, period as 314.28 nm, the duty circle varies from 0 to 1) Fig. 4. Electric field distribution with different duty circles (here the period is 314.28 nm, the thickness is 78.6 nm): (a) is for the duty circle of 0.5 and (b) is for the duty circle of 0.75. 3.Results and discussion Fig. 5. Relationship between Jscenhancement and AAO period (here AAOs duty circle is set as 0.75, AAOs thickness is set as 78.6 nm, and AAOs period varies from 290 to 480 nm). Fig. 6. Relationship between Jsc enhancement and AAO thickness (here AAOs period is set as 314.28 nm, AAOs duty circle is set as 0.75, and AAOs thickness varies from 25 to 175 nm). 3.Results and discussion Fig. 7. Absorption spectrum for a 1000 nm thick Si solar cell with different light trapping structures 3.Results and discussion Fig. 8.