第十章 烧结过程——10.3固相烧结 第十章 烧结过程——10.3固相烧结 3. Solid state sintering Sintering process is completed in a condition without any liquid phase. This is a way to make some materials with very high melting points. 第十章 烧结过程——10.3固相烧结 Simplified model 第十章 烧结过程——10.3固相烧结 1. Preliminary stage 1) Model Ball-surface Two ball with fixed distance Two balls with changed distance 第十章 烧结过程——10.3固相烧结 △L/L0 is the shinkage： Cosθ≈1 第十章 烧结过程——10.3固相烧结 2) Characters x/r＜0.3， △L/L0＜0.06 Growth of necks = mass transfer 第十章 烧结过程——10.3固相烧结 3) Dynamics at preliminary stage x: neck radius, r: ball radius, t: sintering （10-14） 第十章 烧结过程——10.3固相烧结 c: concentration of vacancy 第十章 烧结过程——10.3固相烧结 For a conclusion: For ball-surface model: Due to y≈ρ 第十章 烧结过程——10.3固相烧结 Al203 NaF 第十章 烧结过程——10.3固相烧结 Al203 x/r vs. r—3/5 第十章 烧结过程——10.3固相烧结 Sintering mechanism can be obtained by slope of the line, K? can be obtained by the intercept 第十章 烧结过程——10.3固相烧结 2. Middle stage of sintering The particles are no longer balls. 第十章 烧结过程——10.3固相烧结 Pile up method vs. sintering model 第十章 烧结过程——10.3固相烧结 2. Characters Neck growth Connect pores； Grain growth Porosity: ~5% 第十章 烧结过程——10.3固相烧结 3、Dynamics Pore vol. Porosity Vol. of a tetrakaidecahedron 第十章 烧结过程——10.3固相烧结 Assume l=2r, J is Vacancy diffuse flow 第十章 烧结过程——10.3固相烧结 积分 气孔体积 第十章 烧结过程——10.3固相烧结 第十章 烧结过程——10.3固相烧结 3. Late stage of sintering 1) Model Truncated tetrakaidecahedron 2) Characters Closed pores Obvious grain growth Relative density: 95% 第十章 烧结过程——10.3固相烧结 3. Dynamics rarb 第十章 烧结过程——10.3固相烧结 tf: the time that all pores disappear 第十章 烧结过程——10.3固相烧结 α-A1203, fixed sintered temperature, time vs. relative density 第十章 烧结过程——10.3固相烧结