灰霾天气条件下对材料腐蚀性能的研究 　　第一作者：王佳文 (1993-)，女，武汉大学资源与环境科学学院环境工程专业本科生， 　　通讯作者：胡将军（1963-），男，教授，博士生导师，研究方向：大气污染控制工程， 　　 　　 　　摘 要：频繁爆发的灰霾天气，给人们日常生活带来严重危害。针对灰霾期间污染物浓度高，扩散稀释慢，研究其对材料的腐蚀危害。通过暴露在灰霾大气中的A3钢挂片，研究秋冬两季不同气象条件下，灰霾腐蚀作用的影响因素；并在实验室进行模拟实验。结果表明，水分占主导作用，高浓度的PM2.5在湿润条件下加速腐蚀，SO2与PM2.5协同作用，导致腐蚀明显加剧。 　　关键词：灰霾；PM2.5；水分 　　【中国分类法】：TG172 　　 　　 　　Abstract: The frequent outbreak of the haze weather, brings serious harm to the peoples daily activities. For the high concentration of pollutants during haze, the slow rate of diffusion and dilution, studies the corrosion of materials damage.Through the discovery of A3 steel hanging piece in the haze atmosphere, studied the haze corrosive action influence factors under the fall and winter seasons with different weather conditions. In addition, did some simulation experiment in the laboratory. The result indicated that, the humidity content occupies the leading role, highly concentrated PM2.5 accelerates corrosion under the moist condition. SO2 and the PM2.5 synergistically cause the more severe corrosion. 　　Key words: Haze；PM2.5；Humidity 　　 　　 　　1 引言 　　灰霾产生的原因主要在于城市内部扩散条件有限，冷空气较弱，风速小，城市中的各种悬浮污染物无法及时扩散，并在近地面逐渐积聚，加上气候干旱少雨，日照强烈，湿度较小，污染物之间就容易发生各种光学反应，形成灰霾【1】。 　　 　　近年来，全国灰霾天气频繁爆发。灰霾天气爆发时，常伴随有近地逆温现象，一般都伴有风速低，相对湿度低，日照强烈。这样的气象条件不利于污染物扩散稀释，细颗粒物往往长期滞留在大气层中，进一步发生光反应生成二次污染物。细颗粒物PM2.5中水溶性离子成分相对稳定【2】，质量浓度由高到低主要为SO42-、NO3-、NH4+、Ca2+、K+、Cl-、Na+、Mg2+、F-、当PM2.5沉积在碳钢表面，其自身携带的水溶性离子，以及吸附的酸性污染物等溶于水薄膜后，加速腐蚀【3】。 　　目前，对灰霾天气的研究十分有限。周刚【1】等研究了灰霾的来源及对人体呼吸系统的危害，唐傲寒【4】,F.Wei【5】等对灰霾期间污染物的化学组成及污染特征进行了研究，BRANIS M【6】，姚玉刚【7】等对灰霾的检测技术进行了研究，李洪【8】等对灰霾天气的危害进行了研究。 　　但是对于灰霾天气条件下对材料的腐蚀作用并未有人研究。考虑到几乎所有与大气接触的金属材料都会受到大气腐蚀,大气腐蚀所造成的损失约占腐蚀总损失的一半以上【9】，研究灰霾天气带来的腐蚀危害，不仅对大气环境的保护和污染的治理有很强的现实意义，也会促进对材料防护措施的改进，减少经济损失。 　　2 实验方法及内容 　　实验共分为两部分内容，第一部分为室外灰霾大气中的挂片腐蚀研究，第二部分为室内对腐蚀作用的影响因子的研究。 　　2.1实验材料： 　　 A3碳钢标准腐蚀试片， 尺寸为:50 X 25 X 2mm 　　2.2实验方法: 　　 室外实验方法：将工业污染严重区作为暴露地点(暴露位置与大气检测仪器相距约2m,故暴露处的大气质量可参照该处大气监测点的大气数据)，在距离地面3-4m处，每次平行放置3片A3碳钢挂片于实验架上，完全暴露在大气中，避免雨水直接冲刷。每隔25天，更换一次挂片，同时收集