【2017年整理】纳米二氧化钛的制备及其运用.docVIP

纳米二氧化钛的制备及其运用 姓名：黎燕梅 学号：222012325022069 学院：园艺园林学院 摘要：纳米二氧化钛微粒具有很大的比表面积，其表面面原子数、表面能和表面张力随粒径的下降急剧增加，由于其尺寸的细微化，表现出来独特的物理和化学特征，导致纳米二氧化钛微粒的热、光、敏感特性和表面稳定性等方面不同于常规粒子，这是它在环境、信息、材料、能源、医疗与卫生等领域有着广阔的应用。本文综述了纳米二氧化钛的结构、性质及其制备方法，并介绍了近年来二氧化钛的应用及发展。 关键词：二氧化钛；结构；性质；制备；运用 Preparation and application of nano-sized titanium dioxide Name: Li Yan-Mei Student Nunber: 22201325022069 Academy: Landscape gardening Abstract: As the special physics and chemistry properties of nano-titania that it light, heat, sensitive properties and surface stability were quite different from general materials, they were intensively applied in the environment, information material, source of energy, medical treatment and hygiene etc. The surface atom number ,surface ability and surface tension of nano-titania particles with high surface area were sharply increased along with the digression of the diameter .The properties, constitution, preparation were summarized, and the progress in the application of nano-titania in recent years was described. Keywords: nano-sized titanium dioxide; constitution; character; preparation; application 1.二氧化钛的基本结构 二氧化钛是金属钛的一种氧化物，其分子式为TiO，TiO在自然界中存在三种晶体结构：金红石型、锐钛矿型和板钛矿型，其中金红石型和锐钛矿型TiO2具有较高的催化活性，尤以锐钛矿型光催化活性[4]最佳，其晶格参数a=37.85nm，c=95.14nm, 两种晶型结构如图1-1所示,?可以看出?锐钛矿型和金红石型的晶型结构均由相互连接的TiO2八面体组成，两者的差别在于八面体的畸变程度和八面体间相互连接的方式不同 八面体间相互连接方式包括共边和共顶点两种情况，如图1-2所示 锐钛矿型TiO的单元结构中钛原子处与钛氧八而体的中心，其周围的六个氧原子都位于八面的棱角处，有四个共棱边，也就是说，锐钛矿型的单一晶格有四个TiO分子，锐钛型TiO的八面体呈现明显的斜方晶型畸变，Ti-O轴距离均小且不等长，分别为1.937x10m和1.964x10m，这种不平衡使TiO分子极性极强，从而是其表面易吸附水分子使水分子极化而形成羧基。这种表面羟基的特殊结构使其表面改性成为可能，它可作为广义碱与改性剂结合，从而完成对TiO的表面改性金红石型TiO也为四方晶系，晶格中心为Ti原子，八面体棱角上为6个氧原子，每个八面体与周围10个八面体相联（其中有两个共边，八个共顶角），两个TiO分子组成一个晶胞，其八面体畸变程度较锐钛矿要小，对称性不如锐钛矿相，其Ti–Ti键长较锐钛矿小，而Ti-O键长较锐钛矿型大。板钛矿型TiO为斜方晶系，6个TiO分子组成一个晶胞。? 三种晶相以金红石相最稳定，而锐钛矿和板钛矿在加热处理过程中会发生不可逆的放热反应，最终都将转变为金红石相。 2.纳米TiO的性质 2.1 紫外线防御能力 纳米二氧化钛颗粒吸收紫外线的能力比普通二氧化钛要强得多，再加上它能使光谱中200-400nm的紫外线的到充分散射，因而具有很强的紫外线防御能力。 2.2 表面亲水性 目前研究证明，在光照条件下，TiO表面的超亲水性起因于其表面结构的变化，在紫外线照射下，TiO价带电子被激发到导带，电子和空穴向