帘线钢质量控制技术.pdf

帘线钢质量控制技术 卢玉英王志福 (江苏沙钢集团有限公司张家港215625) 摘要帘线钢对纯净度、表面质量、金相组织等要求十分严格。系统阐述提高帘线钢质量的措施，主要包括选用 合适的脱氧工艺，合理的二次精炼工艺；特殊合金及添加技术；钢水防止AI夹杂污染工艺；中间包冶金；合适的拉 速及二冷配水参数等等。采取以上措施，纯净度明显提高，非金属夹杂物尺寸小于15am，氮化钛夹杂物尺寸小于 4ttm。偏析问题得到改善，拉拔性能明显提高。 关键调帘线钢；纯净度；非金属夹杂；钛夹杂 Control ofSteelforSteelCord Quality Technology Lu Zhifu YuyingWang 215625) (JiangsuShagangGroupCo．．Ltd．Zhangjiagang Abstnct of andmierostructureforstedforcord“estrict．Measuresim· Requirements puritydegree．surfacequality for ofsteel cord deoxidization and provingquality mainlyinelnde叩timumprocess，pfoperrefining．specialalloy adding ofAluminum ofmiddlesteel andsee- technology，preventinginclusion；smeltingcontainer，reasonabledrawingspeed these is andthesizeof is ondary nonmetalinclusioras ccolingparameter．Alteradoptingmeastlr∞．puritydegreeimpmved le∞than andthesizeoffitaniumoxideinclmiomislessthan is and 15ttm 4pm．Segregationproblemimproveddrawing isineremed property evidendy． steelfor Keywords degree；nonmetalinclusion；Titaniuminclusion cord；purity 曲、拉伸等一系列变形，因此对帘线钢的纯净度、表面质量、金相组织等要求极高，尤其是非金属夹杂物，在钢 帘线生产过程中的危害尤为突出。钢帘线在冷拔和捻股过程中发生断丝，最主要的原因之一是钢中存在硬 而不变形的脆性夹杂物11．2l。生产经验表明，夹杂物大于被加工铜丝直径的2％就会导致钢丝在冷拉和合 股过程中脆性断裂L3J。用户在要求提高生产率的同时，对帘线用线材中非金属夹杂物造成的断线敏感性要 求也越来越高。 为满足用户需要，提高产品质量，沙钢对帘线钢生产工艺进行优化。本文系统的介绍了沙钢帘线钢生产 过程中的质量控制技术。 1原辅材料有害元素控制 原辅材料是保证帘线钢质量的前提．入炉铁水、废钢、添加的渣料、台金料等均需对有害元素进行控制。 (1)Cu元素 C