高透明度可溶性聚酰亚胺共聚物的合成与表征 蒋学 1 田秀枝 陆慧 （江南大学纺织服装学院，生态纺织教育部重点实验室（江南大学），江苏无锡，214122） 摘 要 将含有柔性异亚丙基团的4,4-(4,4-异亚丙基二苯氧基）双苯酐(BSAA)与3,3，4,4-二苯醚四酸 二酐(ODPA)共同作为二酐单体与4,4-二氨基二苯砜（DDS）共聚得到含砜基的聚酰亚胺，研究了共聚物在 多种常用溶剂中的溶解性，并检测了共聚物薄膜的可见光透过性能和玻璃化转变温度，探讨了共聚物的溶 解性、光透过性能以及玻璃化转变温度与柔性单体含量之间的关系。 关键词 聚酰亚胺，共聚，溶解性，透过率，玻璃化转变温度 Synthesis and Characterization of Soluble Polyimide with High Optical Transmittance Jiang Xue, Tian Xiuzhi, Fang Kuanjun, Lu Hui （Key Laboratory of Eco-Textiles of Ministry of Education (Jiangnan University), College of Textile and Clothes, Jiangnan Univeristy, Wuxi, Jiangsu, 214122） Abstract A flexible dianhydride was introduced into polyimide in order to produce soluble PI with lower Tg, and the light transmittance of the PI film was tested. It was proved that the introduced flexible isopropylidene could improve the solubility of the polymer and lower the glass-transition temperature. The co-monomer could also weaken the color of PI film and raise the light transmittance. Key Words polyimide ， copolymerization ， solubility ， transmittance ， glass-transition temperature 聚酰亚胺( PI) 具有优良的化学稳定性、耐热性能和机械性能。而且单体来源广泛，种 类繁多，因而在许多领域得到广泛的应用[1-3]。 在PI的各种应用领域，其优良的耐溶剂性能和耐热性能在其应用中是其它材料无可比拟 的优势，但同时又是阻碍其加工的最大缺点。普通PI 难熔融，难溶解，因此由于加工成型 难度较高而限制了其在很多方面的应用。因此，在保持PI 固有的耐热性能及其它优良特性 的同时，降低PI 材料的刚性并增加其在有机溶剂中的溶解能力，降低PI的玻璃化转变温度 以改善它的加工性能，是PI研究的重要课题[4-8]。有许多文献报道了提高聚酰亚胺溶解性以 基金项目：国家自然科学基金（No.； 生态纺织教育部重点实验室（江南大学）开放基金项目（No. KLET0607）。 作者简介：蒋学（1976－ ），男，理学博士，江南大学纺织服装学院副教授。研究方向：功能高分子材料 的合成与应用。 1 转载 及降低其玻璃化转变温度的途径，比如合成新的含氟单体[9]，采用含有醚键的单体以增大聚 酰亚胺主链的柔性[10,11]，含有大的侧基以减弱聚合物分子间作用而降低其结晶性能[12,13]等。 另外，聚酰亚胺常常应用于一些光学器件，有的器件需要PI膜具有较好的光波透过性能， 但目前常用的PI一般都存在颜色，导致对一定波长范围的光线透过率不高，是PI光学材料应 用中有待解决的问题[14-16]。在光学材料方面，砜基的引入可以利用其中S原子的容易诱导极 化的性质，调节聚合物的折射率及双折射率等光学性能[17]。但同时可能会使聚合物的颜色 加深，并且由于主链含有砜基而更加不易溶解或熔融。本文通过在合成含砜聚酰亚胺过程中 引入含有柔顺链的二酐单体，应用不同配比合成可溶性的含砜聚酰亚胺，并表征了聚合物的 热性能。 1 实验部分 1.1 原料 3,3,4,4-二苯醚四酸二酐(ODPA)，分析纯，上海合成树脂厂；4,4-(4,4-异亚丙基二苯氧 基）双苯酐(BSA