 PAGE \* MERGEFORMAT 18 Piercing - Preparation of coagulation bath coixenolide microcapsules Technology 【Abstract】 Objective To investigate the piercing - Preparation of the coagulation bath coixenolide Microencapsulation process conditions, obtained embedding the high rate of good quality coixenolide sensory micro-capsules. Acetone as the solvent extraction method coixenolide; with sodium alginate as wall material, sharp Kong - coagulation bath method Microencapsulation. The results obtained microcapsule orthogonal experiment the optimum conditions: wall material alginate solution, the quality of the initial concentration of 8g / L, core material and wall material Coixenolide the quality of sodium alginate ratio of 0.6:1, emulsifier in the wall material and core material emulsion dispersion of the mass concentration of monoglyceride 0.5g / L and sucrose ester 0.5g / L, the quality of curing liquid CaCl2 concentration of 10g / L. Conclusion of the resultant microcapsules blast drying at room temperature and embedding rate was 80.4%, embedding effect is good. Keywords: coixenolide piercing - coagulation bath Microencapsulation Study on the technology of microencapsulation of coixendide 【Abstract】 Objective To study the technology of microencapsulating coixendide by piercing-solidifying incuber method and to gain production of high retention ratio and good taste.Methods Coixendide was extracted by acetone from coix; sodium alginate was selected as wall-material and coixendide was microencapsulated by piercing-solidifying method.Results According to orthogonal test, the concentration of alginate solution was 8g/L.The ratio of coixendide to alginate was 0.6:1. The concentration of emulsifier MG and SE both was 0.5g / L. The concentration of CaCl2 solation was 10g / L. The emulsification temperature was 50 ~ 60 ℃. Conclusion After microcapsules were dried by blowing under room temperature, the retention ratio of coixendide were 80