消失模铸造EPS泡沫分解过程的三维数值模拟.pdfVIP

学兔兔 Oct．2010 VoI．59 No．10 消失模铸造EPS泡沫分解过程的三维数值模拟 张志莲，肖云峰 (北京石油化工学院，北京100038) 摘要：消失模泡沫分解、析出过程直接影响金属的充型能力，文中采用数值模拟方法，研究了消失模铸造泡沫分解过 程的流体动力学特性，预测了泡沫残留物的产生以及对最终铸件质量的影响，并通过实际发动机缸体进行验证，表明 模拟值与实际测量值基本吻合。 关键词：消失模；数值计算；泡沫分解；充型能力 中图分类号：TG249．6．39 文献标识码：A 文章编号：1001—4977(2010)10—1057—04 Three．Dimensional Sim~ilation of EPS Evaporation Process fo1 hree_ ensi0nal mulatiOn Of 15 rocess for Lost FOam Casting ZHANG Zhi—lian，XIAO Yun—feng (Beijing Institute of Petrochemical Technology，School of Mechanical Engineering， Beijing 1 00038，China) Abstract：FOam evaporation has direct influence on metal filling capability in lost foam casting．The numericaI simulation method was applied to analyze the fluid dynamic characte ristics of the EPS foam evaporization process．The foam residues。positions and their influence on quality of casting were predicted and validated with actuaf engine cylinder．The results show that simulation results matched the practical measure value wel1． Key WOrds：lost foam：numericaI simulation；foam evaporation；filling capability 干砂负压消失模铸造技术 (简称LFC)被称为 为一级，本文采用Favor(fractional area／volume)技术 “铸造工业的绿色革命”。LFC的特点是型腔被泡沫模 对庞大、复杂的发动机缸体进行网格划分为结构化的 样占据，金属液的充型过程实际上是金属液置换泡沫 网格。网格模型如图l所示，对于固壁内部采用矩形结 模样，泡沫模样遇金属液气化分解的过程。因而，泡 构网格，薄壁部位引入多块网格进行局部加密；固壁 沫模样是消失模铸造的关键环节，模样材料种类和密 边界采用面积和体积的百分比模拟复杂形状，同时直 度决定模样分解时的吸热量及分解产物的数量，对金 接把金属液体动力计算限制在单元的开放区域，直接 属液充型能力产生影响，并且影响的显著程度与浇注 将单元的面积和体积百分比作为因子引入有限差分离 温度、过热度及模样厚度有关Il】。因此，利用数值模拟 散计算，大大减小运算规模和时间[21。 对消失模铸造泡沫分解过程的流动场进行数值模拟， 可以定量地了解模样分