球铁油压机油缸的铸造工艺.pdfVIP

学兔兔 球铁油压机油缸的铸造工艺 丁 辉，纪汉成 (金坛市金岗机械制造有限公司，江苏 常州 213242) 摘要：介绍了球铁油压机油缸的铸造工艺，包括过滤浇注系统、冒口及冷铁、排气系统、熔炼 及浇注工艺设计。阐述了采用变径陶瓷管的生产工艺要点，有效地解决了铸件缩孔、缩松、气 孔、夹渣和渗漏等缺陷，提高了铸件成品率，降低了生产成本，取得很好的经济效益。 关键词：球铁；油压机底座；铸造工艺 中图分类号：TG255 文献标识码：A 文章编号：1673-3320(2015)06—001卜04 Casting Process of the Ductile Iron Oil Hydraulic Machine Cylinder DING Hui，JI Hancheng (Jingang Machinery Manufacture Co．，Ltd．，Changzhou 213242，Jiangsu，China) Abstract：Casting process of the ductile iron oil hydraulic machine cylinder has been introduced， including filtering and pouring system，riser and chill，exhaust system，melting and pouring process design．The production process points of using aajustable ceramic tube have been described．The defects of casting shrinkage，porosity,air hole，slag，leakage，etc．，have been solved effectively,and the finished product rate is improved．the production cost is reduced and the economic benefit is obtained． Key words：ductile iron；oil hydraulic machine base；casting process 我公司承接生产的油压机系列球铁件，主要 用于橡胶件的注射成型或真空成型部件，工作过 程中需承受2～10 MPa的压力。其中油缸是油压机 上的重要部件，它要求强度高、韧性好，可靠性 要求高，内腔孔硬度均匀有良好的耐磨性能，同 时要求组织致密、无缩松、无渗漏。 1 油缸结构及技术要求 油缸的结构如图1所示。油缸结构虽然较为 图1 铸件结构 简单，但铸件壁较厚、高度高，要求经过25 MPa 铸件材料牌号为QT5O0—7，净重750 kg， 保压试验30 min无渗漏，铸件不允许有缩松、气 最大轮廓尺寸d~630 mm×880 mm，主要壁厚为 孔、夹渣、裂纹等缺陷。不仅对铸件外观质量要 90 mm，最大壁厚为l20 mm，要求铸件在铸态下 求高，而且底座油缸内腔加工精度、光洁度以及 达到使用性能。铸件的化学成分见表l，铸件的力 对铸件致密度也要求甚高。 学性能、硬度和显微组织要求见表2。 收稿日期：2015—08一10 作者简介：纪汉成 (1966一)，男，总工程师，主要从事铸造工艺、熔炼技术及质量管理工作