低合金钢WC9铸件抗拉强度与洛氏硬度HRB的关系.pdfVIP

学兔兔 低合金~NWC9铸件抗拉强度与洛氏硬度HRB I)~关系 叶永姣，谢小兵 (中核苏阀横店机械有限公司，浙江 东阳 3221 18) 摘要：通过对低合金钢wc9铸件试棒的抗拉强度Rm与洛氏硬度HRB的试验数据的整理计算，发 现抗拉强度Rm与洛氏硬度HRB之间存在正相关性。利用回归方程得出了抗拉强度Rm与洛氏硬度 HRB因子间的关系，该经验公式给铸造生产和应用企业判断低合金~NWC9铸件力学性能合格与否 提供了便利。 关键词：低合金~NWC9铸件；抗拉强度；洛氏硬度；回归方程 中图分类号：TG142．33 1 文献标识码：A 文章编号：1 673—3320(2015)06—001 5—04 Relationship between Tensile Strength and Rockwell Hardness HRB of Low Alloy Steel WC9 Casting YE YongJiao，XIE Xiaobing (Heval Hengdian Machinery Co．，Ltd．，CNNC，Dongyang 322118，Zhejiang，China) Abstract：A positive correlation between tensile strength and Rockwel1 hardness HRB has been found through calculation of experimental data of tensile strength Rm and Rockwell hardness HRB of lOW alloy steel WC9 casting．The relationship between the tensile strength Rm and the Rockwell hardness HRB factor has been obtained by using the regression equation．The empirical formula provides a convenience for the enterprises engaged in the production and application of foundry to judge whether the mechanical properties of low alloy steed WC9 casting is qualified． Key words：low alloy steel WC9 casting；tensile strength；Rockwell hardness；regression equation 1 试验材料和方法 随机抽取公司一段时间日常生产低合金钢 WC9铸件的基尔试块的抗拉强度与对应的洛氏硬 度试验的数据，建立两者问的回归方程式。 带炉号基尔试块的模型是与铸件同等条件下 碱酚醛树脂砂制作，如图1所示。锆英粉涂料涂 刷，基尔试块一模出二，与铸件同炉钢水同等条 图1 基尔试块 件下在铸件浇注过程的中途浇注。做试验的试块 毛坯，从基尔试块上割取 28 X 220试棒，随铸 2 试验数据分析 件同炉进行热处理。热处理后的低合金钢WC9 2．1 散布图 铸件试棒按美标ASTM要求 ( =12．5~0．20 mm， 采用该试验方法获得一系列和抗拉强度Rm和 。：50 mm)机械加工成拉伸试验用的试棒，洛氏 洛氏硬度HRB的实测数据，根据试验数据作散布 硬度HRB在拉伸前检测拉伸试棒的夹持段。 图，如图2所示。 收稿日期：2015—05—26 作者简介：叶永姣 (1973年一)，女，注册质量