屈服 塑性变形 基本常识(国外英文资料) When the stress exceeds the elastic limit, the deformation increases rapidly, and in addition to producing elastic deformation, some plastic deformation is produced. When stress reaches point B, the plastic strain increases dramatically, and the curve shows a small, fluctuating platform, which is called submission. The maximum and minimum stress of this stage is called the upper yield point and the lower yield point. Due to the stability of the lower yield point, it is called the yield point or yield strength (sigma s or sigma 0.2) as a measure of material resistance. Some steel products (such as the high carbon steel) no significant yield phenomenon, usually happen to trace the plastic deformation of the stress of (0.2%) as the yield strength of steel, called the conditions to yield strength The yield strength of the submarine is bound to be dense, and the yield strength of the Q235 is 235MPa. Yield strength, the unit is Pa, such as the sea-wolf HY - 100 grade steel yield strength should be 820 mpa (this is the very high value, for general engineering use of low carbon steel yield strength is 215-275 mpa, such as making the Q215 steel was read 215, the yield strength is 215 mpa) ok, see this unit you should know what is the meaning of the PASCAL!!!! Force/surface product. The expression of stress, you can understand that when stress reaches 820MPa, this kind of steel will yield. The normative language is the material under stress. This stress is the yield point of the material, and the ratio of the stress and material cross-sectional area is the yield strength. That picture, the agricultural road didnt catch up, Ill fix it for you, and the S point is what he said to be the yield point. If I cant see my explanation. The yield strength should be sigma s or sigma 0.2. The former is often used to represent the plastic material, while the latter represents fragile material that is not so obvious in plastic deformation The yield strength is the meta