20种塑料特性(国外英文资料).docVIP

20种塑料特性(国外英文资料) PA66 nylon 66 and nylon 66 typical application: compared to PA6, PA66 is more widely used in automotive, instrument shell and other needs to have impact resistance and high strength requirements of products. Injection molding process conditions: dry treatment: if the material is sealed before processing, it is not necessary to dry. However, if the container is opened, it is recommended to dry in the hot air of 85C. If humidity is greater than 0.2 percent, 105C is required and a 12-hour vacuum drying is required. Melt temperature: 260-290c. The product of glass additive is 275 ~ 280C. The melting temperature should be avoided higher than 300C. Mold temperature: recommended 80C. Mold temperature will affect the crystallinity, and the crystallinity will affect the physical properties of the product. For thin wall plastic parts, if you use less than 40 c mold temperature, the plastic parts of crystallinity will change over time, in order to keep the geometric stability of the plastic parts, annealing treatment is required. Injection pressure: usually at 750 ~ 1250bar, depending on the material and product design. Speed of injection: high speed (slightly lower for enhanced material). Runner and gate: the position of the gate is very important because of the short solidification of PA66. The gate aperture is not less than 0.5 * t (t is the thickness of the plastic). If the heat flow is used, the gate size should be smaller than the conventional flow path because the heat flow can help prevent the material from solidifying prematurely. The minimum diameter of the gate should be 0.75 mm if you use the submerged gate. Chemical and physical properties: PA66 has high melting points in polyamide materials. Its a semi-crystal-crystal material.PA66 can also maintain strong strength and stiffness at higher temperatures. PA66 is still hygroscopic after molding, depending on the composition of the material, the thickness of the wall and environmental conditions. In p