挤压和热处理对Mg-8Zn-1Al-0.5Cu-0.5Mn镁合金显微组织和力学性能的影响（英文）.pdf

Trans. Nonferrous Met. Soc. China 27(2017) 73−81 Effects of extrusion and heat treatments on microstructure and mechanical properties of Mg−8Zn−1Al−0.5Cu−0.5Mn alloy 1,2 1 3 4 1 Shao-zhen ZHU , Tian-jiao LUO , Ting-an ZHANG , Yun-teng LIU , Yuan-sheng YANG 1. Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China; 2. School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China; 3. Key Laboratory for Ecological Metallurgy of Multi-metallic Mineral, Ministry of Education, Northeastern University, Shenyang 110819, China; 4. Shandong Key Laboratory for High Strength Lightweight Metallic Materials, Jinan 250014, China Received 12 December 2015; accepted 1 September 2016 Abstract: The effects of extrusion and heat treatments on the microstructure and mechanical properties of Mg−8Zn−1Al−0.5Cu− 0.5Mn magnesium alloy were investigated. Bimodal microstructure is formed in this alloy when it is extruded at 230 and 260 °C, and complete DRX occurs at the extruding temperature of 290 °C. The basal texture of as-extruded alloys is reduced gradually with increasing extrusion temperature due to the larger volume fraction of recrystallized structure at higher temperatures. For the alloy extruded at 290 °C, four different heat treatments routes were investigated. After solution + aging treatments, the grains sizes become larger. Finer and far more densely dispersed precipitates are found in the alloy with solution + double-aging treatments compared with alloy with solution + single-aging treatment. Tensile p