超细水泥.pdfVIP

AUM 膨胀剂用于自配超细灌浆水泥 孙南屏 王道平 （广东工业大学建设学院，广东，广州，510090 ） 摘要： 试验表明AUM 膨胀剂用于自配超细水泥时的膨胀值与水泥的组成无关，因此可以 近似地认为AUM 膨胀剂在独立工作。在知道基体的收缩率后，即可通过计算，用AUM 膨 胀剂的掺量调整或控制超细水泥的收缩、膨胀性能。 关键词： AUM 膨胀剂 超细水泥 收缩 膨胀 AUM Expansive Agent Used in Compounding Ultra-fine Grouting Cement Oneself SUN Nan-ping ，Wang Dao-ping （Facutly of Construction ，Guangdong Univ. of Tech. Guangzhou 510090，China ） Abstract ：The experiment indicated that the expansion value of AUM expansive agent used in compounding ultra-fine Cement oneself had nothing to do with the cement composition, so the AUM expansive agent being in the independent working can be supposed approximately. After obtaining shrinkage ratio of the pasle matrix, the contraction or expansion characters can be adjustmented and controlled with the AUM expansive agent mixed in the quantity. The above task can be done after a simple computation. Keywords ：AUM expansive agent ultra-fine cement shrinkage expansion 自配超细灌浆水泥成本低、性能易于自己把握和调整。但超细水泥硬化时收缩大，对灌 浆质量极为有害。可用添加膨胀剂来消除收缩的影响。不同膨胀剂与水泥均有一定的适应性， 找出所用的膨胀剂与水泥的作用规律，则可方便的调整和控制膨胀程度，简化施工操作过程。 1 原材料与研究方法 （1）试验用水泥：广州市珠江水泥有限公司生产的粤秀牌42.5R 硅酸盐水泥（旋窑法 生产），代号P.II42.5R，材料的物理性能见表1，化学成份见表2 。超细水泥由商品水泥经球 磨机研磨而成。 表1 水泥物理性能 检验 细度 凝结时间(h:min) 抗压强度(MPa) 抗折强度(MPa) 项目 比表面积 初凝 终凝 3d 28d 3d 28d 2 国标 ≥300m/kg ≥0：45 ≤6：30 ≥22.0 ≥42.5 ≥4.0 ≥6.5 实测值 380 1：55 2 ：30 34.0 59.4 6.3 9.2 表2 水泥化学成份 CaO SiO2 Al2O3 MgO Fe2O3 SO3 Loss 59.07 21.87 6.02 3.44 2.79 2.08 3.82 3