固溶处理对Ni-Cr-W合金碳化物的影响.pdfVIP

Rare Metal Materials and Engineering Available online at www.sciencedirect.∞m Volume 39 , Issue 7 , July 2010 Online English edition of the Chinese language joumal ,;;,ScienceD irect Cite this article as: Rare Metal Materials and Engineering , 2010 , 39(7): 1157-1161. Effects of Solution Heat Treatment on Carbide of Ni-C r-W Superalloy 1 1 Tang Ze ngwu ,2, Li Jinshan1, Hu Rui\ Liu Yi 1, 8ai Guanghai 1 S臼te Key Laboratory o( Solidification Process的g， Norlhwestem PO伊， technil臼I University, Xian 71∞72， Ch的a; 2 Beijing Xinghang Mechanical-Electrical Equipment Factory, Beijing 100074, China Abstract:τbe microstructure features of a kind of Ni-Cr-W superalloy after solution heat treatment at different temperatures c) for various time (10-120 min) were investigated by means of scanning electron microscope (SEM), transmission (1230-1300 o electron microscopy (TEM) and X-ray diffraction (XRD). The results show that the precipitated phases of the alloy after 801ution heat treatment are identified as W-rich fcc 11公C and Cr-rich fcc 11也Qωrbides. The volume fraction of carbides decreases with increasing ofthe 8OIution heat treatment temperature and time. At the 能mp町ature above 1270 oC for 120 min, most of carbides 缸E diS80lved inωthe Ni-matrix , and the carbides dis位ibuting at twin boundaries may be dissolved into the matrix first. MC carbide has 0 no any fixed orientation re1ationship with the Ni-matrix, but the ang1e of M23 C6 (220