四面盒泳透力.pptx

四面盒泳透力 2011.7.11 四面盒泳透力实验目的 预测和评价电泳漆在复杂结构的内部金属表面的涂覆能力。 实验步骤及设备 一，实验步骤 1，如图所示准备4块磷化板，用A至H的字母在板子上做好标识。 2，用胶带包裹该装置，槽液只能通过小孔进入内腔。 3，将小盒放入槽液中电泳。 4，烘烤并记录每一面的膜厚。 详细步骤见如下附件： Box Throw Power Test Preparation Taping on the edge of 4 test panels with 3M magic scotch tape. A face H face Mark the level on A face panel and H face panel to control coating height. Box Throw Power Test Preparation A face H face Space panels 20mm apart using magnetic spacers. Box Throw Power Test Preparation Wrap assembly with masking tape on both side of assembly Box Throw Power Test Preparation Box Throw Power Test Preparation Box Throw Power Test Preparation Wrap the entire assembly with masking tape to form a closed box (to prevent leak) - Recommend to wrap it double with masking tape Box Throw Power Test Preparation Box Throw Power Test Preparation “A” face “H” face Side Bottom Upside Box Throw Power Test Preparation 9cm Anolyte cell (+) Assembly (-) Box Throw Power Test Preparation Box throwpower装置示意图 ﹢ ﹣ Ω 漆膜厚度测量 15cm 5cm 7cm 每块板子在8mm圆孔处选择四个点测量膜厚，距离孔径中心约2cm。每块板子上的测量点尽可能保持一致，所得数据记录在试验室记录本上。 8mm Box throwpower 影响因素1 ◎ 成膜速度越快，泳透力越高。（较高的湿膜阻抗） ◎ 增加湿膜电导率 将伤害泳透率。 — 溶剂 — 小分子量的树脂 — 有机酸 — 较高温度 Box throwpower 影响因素2 溶剂相关举例：BC，PPH(不能被超滤出槽液)影响泳透力. 因素 电压 时间 温度 极比 搅拌 固体分 PH值 颜基比 溶剂含量 泳透力 影响程度 强 中等 中等 中等 轻微 中等 轻微 轻微 依据溶剂种类 结语 谢谢！！！ 2011.7.25