Na2O含量对白云鄂博尾矿微晶玻璃显微结构及力学性能的影响.pdfVIP

NaO含量对白云鄂博尾矿微晶玻璃显微结构及力学性能的影响／李保卫等 ·129 · InfluenceofNa20 on theM icrostructureandM echanicalPropertiesof Glass—CeramicsBasedonBaiyuneboTailing LIBaowei，DU Yongsheng。，ZHANG Xuefeng ，JIA Xiaolin。， CHEN Hua ，DENG Leibo ，ZHAOM ing (1 InnerMongoliaKeyLaboratoryforUtilizationofBaiyuneboMultiMetallicResources，ElectedStateKeyLaboratory， InnerMongoliaUniversityofScienceandTechnology，Baotou014010；2 CollegeofMathematics，PhysicsandBioengineering， InnerMongoliaUniversityofScienceandTechnology，Baotou014010；3 CollegeofMaterialsScience ．Engineering， ZhengzhouUniversity，Zhengzhou45005~) Abstract Highqualityglass—ceramicsweresuccessfullyproducedfrom theBaiyunebotailingandflyashas mainraw materialsbythemethodofmelting．TheinfluenceofNa2O variationonthefabrication，microstructureand propertyoftheglassceramicwasstudiedbydifferentialthermalanalysis(DTA)，?(raypowderdiffraction (XRD)， scanningelectronmicroscope(SEM)andthemeasurementsofbendingstrengths，density，acid-corrosionandalkali— corrosionresistance．Theresultsshowsthatupto8wt ，theincreaseofNa20 contenthasnodistincteffecton the glass-ceramics．ThenthefurtherincreaseofNa20 concentrationmayhindertheformationofwelldispersedpyroxene particlesbypromotingcrystallizationofnephelinephase．Thischangeaffectslittletheresistanceoftheglassceramic toalkali—corrosion．However，thedensity，bendingstrengthandtheresistancetoacid—corrosionofthesamplesdeterio- rateobviouslyatthesametime． Keywords Naz0，glass—ceramics，Baiyunebotailing，microstructure，mechanicalproperties Na2O含量对 白云鄂博尾矿微晶玻璃显微结构及力学性能的影响 李保卫 ，杜永胜 ，张雪峰 ，贾晓琳。，陈 华 ，邓磊波 ，赵 呜 内蒙古科技大学内蒙古 自治区白云鄂博矿多金属资源综合利用重点实验室，省部共建国家重点实验室培育基地，包头 014010； 2 内蒙古科技大学数理与生物工程学院，包头 014010；3 郑州大学材料与工程