粉煤灰混凝土力学性能探究.doc

粉煤灰混凝土力学性能探究【摘要】本文进行了粉煤灰混凝土的抗压、抗折强度试验，研究了掺入粉煤灰含量不同的粉煤灰混凝土的抗压、抗折强度，结合试验数据分析得出混凝土的抗压和抗折强度都随着粉煤灰掺量的增加，而逐渐的下降，但是粉煤灰掺量在30%以前对混凝土的抗折和抗压强度影响不大。? 【关键词】粉煤灰；混凝土；抗压强度；抗折强度?? Experiment Research on Mechanics Properties of Fly-ash Concrete? Liu Yong-gan?1,Gao Yan-qing?2,Xu Yong-qiang?2,Wang wei?1? (1.Jiangsu Institute of Geology and mineral ResourcesXuzhouJiangsu221006? 2.Airfield Engineering Department,Xuzhou Airforce CollegeXuzhouJiangsu221000) ? 【Abstract】In this paper,an experiment on compressive and anti-break strength of fly-ash concrete are performed.According to the test results, with the increasing of the fly ash added, the compressive and anti-break strength of the concrete would be decreased. Before the content reach 30%, the fly ash has a little influence on the compressive and anti-break strength.? 【Key words】Fly-ash;Concrete;Compressive Strength;Anti-break Strength?? 我国煤炭资源丰富，能源生产以火力发电为主，是粉煤灰排放大国。从1986年的4228万吨到1996年的1.4亿吨，再到2000年的1.6亿吨，预计到今年粉煤灰排放量将达到2亿吨，我国粉煤灰排放量迅速增长。本文研究了掺入粉煤灰含量不同的粉煤灰混凝土的抗压和抗折强度，揭示了不同掺量的粉煤灰混凝土强度的发展规律。? 1. 试验研究? 1.1试验用原材料 （1）水泥：中联P.0 42.5R硅酸盐水泥 （2）粗细集料：细度模数为2.45的天然中砂，5～20mm连续级配的碎石 （3）粉煤灰：徐州矛村电厂的Ⅱ级粉煤灰，氧化硅占54.88% ，氧化铝占32.12%，氧化钙占1.93%，氧化镁占1.45%，氧化硫占0.5% ，氧化铁占4.28%，烧失量2.0%。其各项性能见表1 （4）水：自来水。? 1.2试验方法 建筑用砂GB/T14684-2001，建筑用碎石GB/T14685-2001，用于水泥和混凝土中的粉煤灰GB1596-1991。不同粉煤灰掺量混凝土分别做12个试件，分为两组，一组养护7天，另一组养护28天，每组各有3个抗压试件(150×150×150mm)和3个抗折试件(100×100×400mm)。粉煤灰性能参数见表1。? 2. 试验配合比设计与试验结果? 本试验采用等量取代法进行试验，取水胶比为0.5，Ⅱ级粉煤灰掺量分别为0、10%、20%、30%、40%、50% 试验试验结果见表2和表3。? 3. 试验结果分析? 7d龄期时掺量为10%、20%的粉煤灰混凝土抗压强度略有下降，掺量为30%、40%的粉煤灰混凝土抗压强度有一定程度下降，掺量为50%的粉煤灰混凝土的抗压强度有很大程度下降。掺量为10%、20%的粉煤灰混凝土的抗折强度略有下降，掺量为30%的粉煤灰混凝土的抗折强度有较大下降，掺量为40%、50%的粉煤灰混凝土有很大程度下降 28d龄期时，掺量为10%、20%的粉煤灰混凝土抗压强度有较小下降，掺量为30%、40%的粉煤灰混凝土抗压强度有较大下降，掺量为50%的粉煤灰混凝土的抗压强度有很大程度下降。掺量为10%的粉煤灰混凝土的抗折强度没有变化，掺量为20%、30%的粉煤灰混凝土抗折强度有较小下降，掺量为40%的粉煤灰混凝土的抗折强度有较大下降，掺量为50%的粉煤灰混凝土的抗折强度有很大程度下降。? 4. 结论? 由以上分析结果可知，掺加40%的粉煤灰后，基准混凝土的强度有所降低，但是7天的抗压强度及抗折强度的降低率比28天的降低率要高很多，这样的结果与粉煤灰的性