不同真空热压烧结制程温度对cr50ti50 合金其显微组织与材料特性之 .pdfVIP

不同真空熱壓燒結製程溫度對Cr50Ti50合 金其顯微組織與材料特性之影響 Effect of Vacuum Hot-Press Sintering Process Temperature on the Microstructure and Material Characteristic of Cr50Ti50 Alloys 1 2 2 2 S.H. Chang P.Y. Chang, C.Y. Chang, C.L. Li (Cr-Ti alloys) Laves Th i s stu dy focu sed on det er m in in g TiCr2 the effect of Vacuum Hot-Press Sintering Process temperature on the microstructure and material characteristic of Cr50Ti50 alloys. We con du ct ed num er ou s m anu factur in g Cr 50 Ti 50 exp er im en t s u n der a ser i e s o f different hot-press sintering temp erature from 1,250 to 1,390( 1,250, 1,300, 1,350 and 1,390, resp ectively) . We ob served th e m icr ostru ctur es an d det er m in ed th e mechanical and electric characteristics of 20 MPa th ese m anu factur ed Cr50Ti50 alloy s. Our (1250 1300 1350 1390 ) Cr50Ti50 experimental results showed that the optimal manufacturing parameters were 1,250at 20 MPa 20 MPa for 1 h of hot-press sintering. The 1 1250 optimally manufactured alloys had a relative 95.67% 1.35 104 density reaching 95.67% and an electrical S cm-1 conductivity 1.35 104 S·cm-1. 關鍵詞： Key words: C r - T i A l l oy , H o t - P r e s s S i n t e r i n g , E l e c t r i c Conductivity 一、前　言 (1400~