2205双相不锈钢在淡化海水中的点蚀行为.pdf

14 2 2017 2 EQUIPMENT ENVIRONMENTAL ENGINEERING 11 2205 RO 2205 60~90 1.6 2205 RO 80 RO 1 d 28 d 2 µA/cm2 2 41 d 12 µA/cm 2205 RO Cl– DOI 10.7643/ issn.1672-9242.2017.02.003 TJ04 TG172.5 A 1672-9242(2017)02-0011-08 Pitting Corrosion Behaviors of 2205 Duplex Stainless Steel in Desalination Seawater GAO Li-fei1,2, DU Min1,2 (1.College of Chemical Engineering, Ocean University of China, Qingdao 266100, China; 2.Key Laboratory of Marine Chemistry Theory and Technology, Ministry of China, Qingdao 266100, China) ABSTRACT: Objective To study pitting corrosion behaviors of 2205 duplex stainless steel in level 1 reverse osmosis desalina- tion seawater, natural seawater and concentrated seawater. Methods Open circuit potential, alternating-current impedance, anode polarization curve and electrochemical frequency modulation (EFM) were used to study pitting corrosion behaviors of 2205 duplex stainless steel in different water (level 1 reverse osmosis desalination seawater, natural seawater and 1.6 times concen- trated seawater) at different temperature (60~90 ). Results The EOCP of 2205 duplex stainless steel changed to negative with the temperature increasing in level 1 reverse osmosis desalination seawater. In level 1 reverse osmosis desalination seawater at 80 , the trend of pitting corrosion was found in the 1st day, and stable pitting occurred in the 28th day. The turbulent current of