材加 机枇： 2007年第6期 裂纹对木梁承压与抗弯强度的影响 杨小军，孙友富，昊淼，张涛 (南京林业大学木材工业学院，南京 21 0037) 摘要：设计了裂纹木梁的承压与抗弯性能试验，研究了裂纹对木梁强度的影响。结果表明：裂纹对横 纹承压强度的影响较小，对抗弯强度影响较大；在承压面为50mm X 50mm时木材自身的变异性影响较 小；试件长度≥1 50mm时，局部长度承压值趋于稳定；上下表层横向裂纹使抗弯强度降低近一半。 关键词：裂纹木梁；弯曲性能；横纹承压 中图分类号：$781 文献标识码：A 文章编号：1 OO1—036X(2007)06一O01 1一O3 Influence of the crack on compressive and bending strength of a wood beam YANG Xiaodun，SUN YDu—fu，WU Miao，ZHANG Tao (Nanjing Forestry University，Nanjing 210037，China) Abstract：Experiments on the crack wood beam compressive and bending features have been done、Influence of cracks on wood beam performances are studied．Results show that cracks have little influence on compression，but large on bending strength；Variability in wood is little at compressive face 50mmx5Omm；Compressive strength of partial length tend to stabilize when the length of sample is 1 50mm；Compressive strength of wood beam will be reduced to a half by cracks of surface layer and bottom layer of the beam． Key words：crack wood beam；bending feature；compression 在设计以木材为主体结构的建筑时，要特别关注 材料：樟子松(Pinus sylvestris)，产地东北，含水 木梁或托梁对强度的要求，因其不仅承载来自屋盖的重 率12．25％，有少数活节，一等材。 量，而且还承载来自柱或墙骨柱的横纹压力。在对木梁 设备：微机控制万能力学试验机，型号WDW3050，中 进行材料强度校核时，不能忽视其存在的初始裂纹及使 科院长春科新公司测试仪器研究所制造；木工圆锯机等。 用中出现的裂纹，因为裂纹的出现不仅会破坏木材的完 1．2试验方法 整性，也会降低木材的力学强度，直接关系到设计时安 1．2．1承压试验 全系数的选择。为此笔者从裂纹木梁的承压比例极限及 按试验设计尺寸 (幅面尺寸如图1，厚度皆为 抗弯强度人手进行试验研究，以避免木梁在服役中发生 50ram)制作试件，保证截面上无髓心和钝棱，在承压范 意外，这将有助于木梁的合理设计与使用。 围内无木节，无水平方向或斜向裂缝，木材年轮的弦线 1试验材料与方法 与试件截面底面的夹角小于15。，之后在承压试件背面 1．1材料与设备 中间预制纵向通透裂纹，断面尺寸为5ramx 5ram。最后 按图中设计位置在力学试验机上进行试验，每组试验数