超疏水薄膜制备技术及其性质之研究 - 成功大学.pdfVIP

第二屆資源工程研討會論文集 超疏水薄膜製備技術及其性質之研究 1 2 3 黃宏欽 、向性一 、梁明在 摘要 物體表面經過適當的表面處理成撥水性並具有自我清潔的效果，在奈米科技時代已經引起廣泛的研究。本 研究以奈米級軟鋁石 (boehmite ，20nm)及二氧化鈦 (anatase ，6nm)為表面粗糙度的來源，藉由兩種不同大小的奈 米顆粒互相混合，進而提升其自潔效果。目前結果顯示，添加特定比例的二氧化鈦樣品的確可以降低滑動角， 提升自潔效果。當二氧化鈦添加體積比為軟鋁石的 0.3倍時，其接觸角可高達 167° ，滑動角小於5° 。 關鍵詞 ：撥水、自我清潔。 ABSTRACT To obtain a surface with water-repelling and self-cleaning ability attract much interest in nanotechnology age. Our study focus on coating a hydrophobic polymer on nano-scale boehmite surface to obtain hydrophobic nano-particles via surface modification. We focus on the influence of surface roughness on wetting angle, boehmite nanoparticle(20nm) were used to form different surface roughness. Based on Furnas model, to increase the micropore ratio of the coating, we also empolyed titanium oxide nanoparticle(6nm) into boehmite. When TiO2/boehmite volume ratio is 0.3, wetting angle is 167∘ and sliding angle is less than 5∘ Keywords ：water-repelling, self-cleaning. 1國立成功大學資源工程所碩士班研究生 2國立成功大學資源工程所副教授 3 義守大學化學工程學系副教授 202 第二屆資源工程研討會論文集 入重量比 6wt％ Zonyl 8740(杜邦公司) ，隨即以超音 一、前言 波處理 30 分鐘之後利用磁攪拌子攪拌3 小時即可得疏 在自然界中，生物的微結構扮演著極重要的角 水塗料。 色，近幾年來由於奈米科技的蓬勃發展，利用奈米科 另外稱取軟鋁石與二氧化鈦 (TiO2, anatase)重量比 技來模仿生物的微結構 (仿生學 也已經引起廣泛的研) 分別為 8 ：0 、6 ：2 、4 ：4 、2 ：6 、0 ：8依相同方式製 究，結合表面奈米級的粗糙度及低極性的化學物質 (如 備具光觸媒效應之疏水塗料。 飽和的長碳鏈，其中以全氟烷基 (perfluoroalky)的極性 本研究採用玻璃及氧化鋁基板，於使用前將基板 最低 )使物體的表面具有超疏水（水滴的接觸角高達 置入 0.1M HCl 與 99.5酒精體積比為 1 ：1的混合溶液 150 度以上）與自我清潔的效應。雖然許多物體都具