Influence of Chemical Composition and （化学成分和的影响）.pdf

Metal Forming Influence of Chemical Composition and Tempering Treatment on Toughness of Bainitic 38MnV7 Steel Lucía Rancel1), Manuel Gómez1), José-María Cabrera2), Sebastián F. Medina1) 1) National Centre for Metallurgical Research (CENIM-CSIC), Av. Gregorio del Amo 8; 28040-Madrid, Spain, smedina@cenim.csic.es 2) Department of Materials Science and Metallurgical Engineering, ETSEIB, UPC, Av. Diagonal 647, 08028-Barcelona, Spain. Abstract . This work studies the influence of Mn and the V/N ratio on the toughness of 38MnV7 steel. Four steels with different Mn, N and Ti contents were studied. Lowering the Mn content to approximately 1.5% considerably enhanced toughness by reducing Mn segregation and consequently achieved a more uniform bainitic microstructure. Raising the N content to reach a V/N ratio of close to 5 enhanced the intragranular nucleation of bainite and thus also improved toughness. Isothermal transformation prevented the presence of retained austenite and allowed a complete bainitic transformation. One of the steels contained Ti to control austenite grain growth by the precipitation of TiN particles. However, the results showed that the presence of nanoparticles TiN did not improve the bainitic microstructure. In sum, the work has allowed the obtainment of a 38MnV7 steel with a toughness value (obtained in a Charpy V-Notch impact test) of close to 40 J, and higher than 50 J after tempering at 600 ºC. The steel shows a toughness of close to 20 J at -40 ºC. The optimal composition of the steel (in wt. %) was approximately: C=0.38; Mn=1.53; V=0.11; N=0.0217. Keywords: Bainite, yield strength, toughness 1.INTRODUCTION 2.