高硬度耐磨损电弧喷涂涂层研究-材料工程.PDF

27 Research of High Hardness and Wear Resistance Arc Sprayed Coatings 1 2 1 1 1 , , , , ( 1 , 100022; 2 , 100080) 1 2 1 FAN Jian-jun , QIN Hao , LI Zhuo-xin , 1 1 JIAN Jian-min , SHI Yao-wu ( 1 College of Materials Science and Technology, Beijing University of T echnology, Beijing 100022, China; 2 Beijing Jindahao Surfacing Metal Materials incorported Co.Ltd., Beijing 100080, China) : JCW-B , Ni60 JCW-B , 4%, HV0. 1 1200, 50MPa, XRD Fe B , 3 : JCW-B ;; Fe B; ; 3 : T 174. 44 : A : 1001-4381( 2008)02-0027-04 Abstract: High hardness and wear resistance coating JCW-Bwere deposited via arc spraying. T hem-i crostructure, porosity, hardness, bond strength and abrasion behavior of JCW-B coating was ana- lyzed, the erosion resistanceproperties of coating was compared with Arc Spray Welded Ni60 coating. Results showed that JCW-B coating exhibited dense microstructure, low porosity, high hardness, high bond strength and excellent abrasive and erosive wear resistance. XRD spectrum of the coatings indicates that Fe3B was contained as the main hard phase, which dispersedly strengthens the coatings. Moreover, some Fe2O3, FeO were also formed during the spraying process. It was concluded that FeB3 randomly distributed in the microstructure of coating act as hard phase promoting wear proper- ties. Key words: JCW-B coating; high hardness;Fe3 B;dispersed strengthening; wear resistance , ,,