水利工程建筑物砼外观控制措施 摘要：水利工程建筑物是建筑群体中的一类，是所在地环境的一个有机组成部分。随着经济社会的发展，其外观越来越受到重视。外观设计的质量表现在建筑物满足运行功能要求的情况下，既方便施工，又具有特色。施工的质量表现在建筑物的实施效果。常见的外观质量缺隙主要有蜂窝麻面、色泽不一、气泡偏多，应从施工工艺、建筑材料的质量等方面加以控制。 关键词：水利工程 砼外观；控制措施 中图分类号： TV 文献标识码： A 文章编号： Abstract: water conservancy project building is one kind of building groups, and one of the local environment organic component. Along with the development of society and economy, its appearance more and more attention to. Appearance design of quality performance in the building to meet operation function requirements of the situation, which is convenient for construction, and features. Construction quality performance in building the implementation effect. The appearance of the common quality lack of gap mainly cellular pits, colour and lustre is differ, bubble partial more, should from the construction technology, construction of the quality of the material aspects control. Keywords: water conservancy project， concrete appearance; Control measures 水利工程建筑物是社会各建筑群体中的一类，是所在地环境的一个有机组成部分，随着我区开发步骤的加快，原来地理位置偏僻的水利工程建筑物，现已逐步进入城市居民的视野，这必然导致水利工程建筑物的外观越来越受到重视。 1、常见砼外观质量缺陷及可能产生的原因 （1）表面蜂窝、麻面及气泡 其可能产生的原因：模板表面粗糙或者清理不净；脱模剂涂刷不均匀，拆模时砼粘皮；砼施工配合比计量有误，配比中砂率偏小，粗骨料含量偏大，水泥砂浆过少，或砼坍落度太小；砼搅拌时间不足，拌和不均匀；振捣时间不足或漏振；砼稠度太大，振捣时间过长，模板拼缝处水泥砂浆流失；浇筑高度太高、导料入仓措施不到位，引起粗骨料与砂浆离析。 （2）色泽不一 其可能产生的原因：砼强度较低、成型界面的隔离剂使用不到位，致使局部浅层砂浆薄层在拆模瞬间脱离母体，形成局部浅层剥落；模板隔离剂掺杂，涂抹厚度不一；模板表观糙率不一，反光效果不同；入仓混合料的骨料清洗不净，拌和质量控制不一。 （3）对穿螺栓洞及砼表面缺陷修补引起色差 其可能产生的原因：未用原施工配合比及各类组料拌制砼修补。 （4）砼的缺角、掉边 其可能产生的原因：脱模时操作不当，造成边角损伤。 2、水工建筑物砼外观质量的控制 1.模板质量的控制 结构砼的施工，能否达到工程整体美观的要求，首先取决于模板质量的控制。砼的平整度、光洁度、色差度都与模板质量直接相关。因此，在模板工程的设计、制作时，首先应满足模板结构的强度和刚度，稳定性及整体拼装后的平整度，确保模板拼缝严密、不变形、拆卸方便；其次，要选择好板面材质，并使其同砼脱模剂相匹配。 2. 浇筑工艺质量的控制 （1）原材料 清水砼要求颜色一致，因此选用同一厂家、标号、品种的水泥，使用颜色纯正、安定性和强度好的普通硅酸盐水泥；粗骨料选用强度高、连续级配好、同颜色和不带杂物的碎石，要求定产地、定规格、定颜色。细骨料选用中粗砂，不得含有杂物，要求定产地、定砂子细度模数、定颜色。外加剂要求定厂商、定品牌、定掺量，严格按试验确定的配合比投料。 （2）配合比 砼配合比特别是水灰比的大小是影响砼外观质量因素之一。实践表明同一部位，同一标号的砼，如原材料计量或水灰比产生波动，砼外表存在着明显的色差变化。故在砼生产过程中，要定期检查搅拌计量装