材料取样大全（Materials sampling）.doc

材料取样大全（Materials sampling） Main raw materials inspection standards and sampling methods Sampling test of reinforcing bar (I) reinforcing bar 1., inspection standards: steel raw material test should be the same factory, the same furnace number, the same specifications, the same delivery state, the same approach time, each 60t for a batch of acceptance, less than 60t, also according to a batch of acceptance calculation. 2. sampling quantity: a set of samples (2 tension, 2 cold bending, 1 Chemical) in each batch. For low carbon steel hot rolled discs, the tension is 1. 3. sampling methods: 1 test pieces from interception: every two bars reinforced interception of a tension, a cold one, then a chemical interception specimen, hot-rolled carbon strip cold bending specimens should be taken from different disc. (25/45,30/50) The specimens in each bar from the end is not less than 500mm interception. The tensile specimen length: 7d0+200mm. The cold bending specimen length: 5d0+150mm. The chemical specimen sampling method: 1) analysis chips can be planed or drilled. Before taking the chip, the surface oxide scale shall be removed. 2) the 1/2 symmetrical plane is drawn from the whole cross section of the rolled material or not less than the cross section. 3) perpendicular to the longitudinal axis of drill steel scraps, the depth should be steel axis. 4) a steel chip for verification and analysis must have enough weight. (two) cold drawn steel bars shall be composed of a grade of not more than 20t and a cold drawn steel bar of the same diameter. A batch of 3 steel bars shall be taken from each batch, and each of the 3 specimens shall be subjected to tensile cold bending test. (three) cold drawn low carbon steel wire The mechanical properties of steel wire shall be 1. grade a zhupan test, from each end of an office plate steel wire not less than 500mm and then take two samples respectively, tension and bending experiment, and to determine the disk group according to the tensile