科技创新汽车用滑石填充聚丙烯的力学性能.pdfVIP

学兔兔 摘要：滑石填充聚丙烯是汽车工业中应用最多的改性聚丙烯材料，能达到改善其性能的目的。文章介绍了聚丙烯材 料加入10％，20％，30％，40％滑石填充后的力学性能变化规律，采用试验研究的方法，按照国家标准对其密度、 拉伸强度、弯曲强度及冲击韧性等性能进行了测定。结果表明，随着滑石含量的增加，滑石填充聚丙烯的密度不 断增大；当滑石含量达到30％，滑石填充聚丙烯的拉伸强度和 中击韧性达到最大值；当滑石含量达到20％时，滑 石填充聚丙烯的弯曲强度达到最大值。 关键词：滑石；聚丙烯；力学性能；汽车工业 Mechanical Properties of Polypropylene Modified with Packed Talcum Powder for Automobiles Abstract：Polypropylene with packed talcum powder is the most widely used polypropylene material in automobile industry and it can improve the mechanical property of polypropylene materia1．This paper introduces the changing rules of the mechanical property of Polypropylene Modified with Packed Talcum Powder of 10％，20％，30％ and 40％ respectively．The density,tensile strength，flexure strength and impact strength of the materials are tested according to the GB standards．The results show that the value of density is raised with the rise of Talcum．The tensile strength， impact strength reach maximum respectively when the talcum powder is 30％．At the same time，flexure strength reaches maximum when the talcum powder is 20％． Key words：Talcum；POlypr0pylene；Mechanical properties；Automotive industry 聚丙烯材料一直是汽车制造工业青睐的塑料材料 4)注塑机：海天注塑机厂； 之一，由于其存在着耐低温冲击性差、易老化、吸湿 5)力学试验机：广州试验仪器厂； 性小及易发生融体破裂等缺点【1】，所以汽车工业中经 6)冲击试验机：长春试验机有限责任公司。 常用价格低廉和化学性能稳定的滑石填料来填充聚丙 1．2试验步骤 烯，形成三元复合体系[2-6] 以达到增加强度、增加 将一定量的PP和滑石粉混合均匀后，加入一定 韧性及改善性能的目的。文章采用试验研究的方法， 的增韧剂，在烘箱中干燥一天；然后放入双螺杆挤出 在聚丙烯材料加入质量分数为10％，20％，30％，40％ 机中挤出造粒，放入烘箱干燥2天；最后放入注塑机 的滑石进行填充，按照国家标准对其密度、拉伸强度、 中注塑成标准样件，测试力学性能。 弯曲强度及冲击韧性等性能进行了测定。分析了具体 1．3试验依据 的试验数值和试验曲线，总结了滑石材料对聚丙烯的 1)密度：GB／T 1033--1986(塑料密度和相对密 力学性能的影响。 度试验方法)； l 试验