the effect of ageing time on some mechanical properties of aluminum0.5% glass reinforced particulate composite老化时间的影响在一些玻璃aluminum0.5%增强颗粒复合材料的力学性能.pdfVIP

下载本文档

1
0
约2.75万字
约 5页
2017-08-29 发布于上海
举报
版权申诉

the effect of ageing time on some mechanical properties of aluminum0.5% glass reinforced particulate composite老化时间的影响在一些玻璃aluminum0.5%增强颗粒复合材料的力学性能.pdf

1、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。。
2、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
3、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
4、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
5、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
6、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
7、VIP文档为合作方或网友上传，每下载1次，网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档

the effect of ageing time on some mechanical properties of aluminum0.5% glass reinforced particulate composite老化时间的影响在一些玻璃aluminum0.5%增强颗粒复合材料的力学性能

Journal of Minerals and Materials Characterization and Engineering, 2012, 11, 919-923 Published Online September 2012 (http://www.SciRP.org/journal/jmmce) The Effect of Ageing Time on Some Mechanical Properties of Aluminum/0.5% Glass Reinforced Particulate Composite 1* 2 3 4 Aondona P. Ihom , Nyior G. Bem , Emmanuel E. Anbua , Joy N. Ogbodo 1Department of Metallurgy, National Metallurgical Development Center, Jos, Nigeria 2Department of Metallurgical and Materials Engineering, Ahmadu Bello University, Zaria, Nigeria, 3Department of Mechanical Engineering, Federal Polytechnic Bauchi, Bauchi, Nigeria 4Department of Welding and Fabrication, Scientific Equipment Development Institute (SEDI), Enugu, Nigeria * Email: paulihom@yahoo.co.uk Received June 23, 2012; revised July 31, 2012; accepted August 22, 2012 ABSTRACT A particulate-hardened composite usually known as cermets with aluminum matrix and reinforced with ceramic parti- cles from broken bottles was used to investigate the effect of ageing time on hardness and tensile strength. The samples used for the work were produced using stir-cast method and the samples were cast in metal moulds to improve on the surface finish and to obtain good cooling rate. The composite composition used was Al/0.5% glass particles. The sam- ples were treated at 500˚C and quenched in water at 65˚C. They were then aged at various temperatures ranging from 150˚C - 210˚C. The result of the hardness test showed that within the range of the ageing time selected the hardnes