稀土氟化物上转换发光材料的制备.docVIP

编号 本科生毕业Preparation of Rare Earth-Doped Fluorides on the upconversion of luminous materials 学 生 姓 名 郭军军 专 业 化学工程与工艺 学 号 0407113班35号 指 导 教 师 闫景辉 学 院 化学与环境工程学院 2008年06月 摘 要采用十六烷基三甲基溴化铵/第二辛醇/水或盐溶液微乳液体系法制备出BaF2:Yb3+,Er3+纳米上转换发光材料。通过X射线衍射（XRD）确定了所制备样品的结构，样品的粒径均在纳米范围之内的形貌nm。用荧光光谱仪进行测试，发现BaF2:Yb3+,Er3+纳米微粒在1540nm（4I13/2→4I15/2）出现了发射峰。Yb3+,Er3+ 配比对上转换发光强度的影响。 关键词：上转换发光 纳米氟化物 微乳液 稀土离子 ABSTRACT This dissertation briefly outlined the rare-earth ion doped fluoride on the history of upconversion of luminous materials, and study the status and development prospects. Use cetyltrimethylammonium bromide (CTAB) /The second octanol/ water (or salt solution) microemulsion system prepared the BaF2: Yb3+, Er3+ nano-conversion luminous materials. X-ray diffraction (XRD) determined by the structure of the sample, and use the Debye-Scherrer equation to Calculate the sample size, the results showed that both in its size within the scope of nanotechnology,On the conversion of nanoparticles for spherical shape, size of about 21 nm. By fluorescence spectrometer for testing and found that BaF2: Yb3+, Er3+ nanoparticles in the 1540 nm around (4I13/2 → 4I15/2) in the emission peak. At ordinary temperature with 980 nm laser excitation samples, samples sent red and green, and discussed the impact about the different ratio Yb3+, Er3+ to the luminous intensity of upconversion. Key words: Upconversion luminescence; Fluoride nanoparticles; Microemulsions; Rare-earth ions 目 录 摘 要 II ABSTRACT III 目 录 IV 第一章 绪 论 1 1.1 引言 1 1.2 上转换发光材料的概念 2 1.3 上转换发光材料的发展概述 3 1.4 掺稀土纳米发光材料 4 1.4.1 掺稀土纳米发光材料的制备方法 4 1.4.2 纳米材料的结构测试方法 5 1.4.3 纳米发光材料的应用 6 1.4.4 纳米发光材料的发展趋势 7 1.5 微乳液法制备纳米材料 7 1.5.1 微乳液法制备纳米材料的特点 7 1.5.2 微乳液法制备纳米材料的结构和性质 7 1.5.3 微乳液法制备纳米材料的影响因素 8 1.6 微乳液法制备纳米材料的机理 9 1.6.1 微乳液作为纳米反应器的原理 9 1.6.2纳米材料的形成机理 10 1.6.3影响微乳法制备纳米粒子粒径的因素 11 1.7 无机固体氟化物的特性 11 1.7.1氟化物特殊的化学及物理性质 12 第二章 上转换发光的相关理论 14 2.1 稀土元素 14 2.1.1 稀土元素的主要物理化学性质 14 2.1.2 稀土离子的能级 16 2.1.3 稀土离子的f-f跃迁,f-d跃迁和电荷迁移带 17 2