蒸压灰砂砖（autoclaved sand-lime brick）.docVIP

蒸压灰砂砖（autoclaved sand-lime brick） Autoclaved lime sand brick (autoclaved sand lime brick) is a kind of lime, sand, quartz sand tailings as the main raw material, made by mixing with water, digestive reaction, pressing, steam pressure curing wall material. The bricks by autoclave high temperature autoclave, a kettle after natural curing after 28 days, the strength can reach above MU10.0, has been widely used in masonry bearing wall and frame multilayer infill wall, standard brick has been applied to 0 + basis, following the line of the sewer and other parts. Autoclaved lime sand brick with high strength, low loss, shrinkage rate is relatively small, appearance standard, convenient construction, masonry wall after the high flatness, saving plastering mortar, is a kind of ideal wall material. But it also has the characteristics of slow water absorption, slow water yield, dry shrinkage and more than clay brick, so it should be noticed during construction. According to the current construction site use steam practical problems commonly existed in pressing brick, puts forward some technical points to grasp (according to the construction sequence of writing). 1 masonry mortar. More than 0 or more load-bearing walls should be used not less than M7.5 of mixed mortar masonry, frame filled wall, the use of M5 and above mixed mortar masonry. Lime paste should be used in mixing mortar, which can increase the strength at the later stage of the wall. The lime block must be aged for 14 days to prevent explosion of ash due to lack of aging time. Should not use the lime king and other additives, because it is the main component of micro expansive agent, mortar strength will cause more and more low, and even become the strength of the mortar strength; it is not easy to use lime powder bags, such as lime powder bags must be used when the curing time should be more than 3 days. The following 0 + brick foundation should be M10 and above the cement mortar and autoclaved lime sand brick, c