废钢铁标准摘要（Scrap steel standard Abstracts）.docVIP

废钢铁标准摘要（Scrap steel standard Abstracts） 2005-03-09 09:01 By the State Administration of quality supervision, inspection and quarantine, the National Standardization Management Committee issued by the new revised scrap iron and steel national standard (GB4223-2004) issued by the approval, formally implemented since December 1, 2004. Part of the summary is as follows: 4 Classification Waste iron and steel are divided into two categories: scrap iron and scrap steel. 4.1 scrap iron 4.1.1 the carbon content of scrap iron is generally greater than 2%. The sulphur content (mass fraction) and phosphorus content (mass fraction) of quality scrap iron are not greater than 0.07% and 0.40%, respectively. The sulfur content (mass fraction) and phosphorus content (mass fraction) of common scrap iron and alloy scrap iron are not greater than 0.12% and 1% respectively. The iron content of blast furnace additions shall be no less than 65%. 4.1.2 scrap iron is divided into smelting scrap metal and non smelting scrap metal by its use. 4.1.2.1 smelting scrap metal 4.1.2.1.1 smelting scrap iron is classified according to quality and shape, as specified in table 1. Table 1 Classification of scrap metal for smelting Typical examples of varieties and categories Code A B C High quality iron 101 length less than 1000mm, width less than 500mm, the height of less than 300mm, single weight less than 200kg by crushing, fusing easily become a kind of shape of raw iron (iron scrap iron chips turning down at the end of the cold pressing and mixing with body) block transmission engineering machinery parts, iron castings, cast iron roll, the car body, the engine shell, ingot mould etc. Ordinary iron 102 cast iron pipes, high phosphorus iron and high sulfur iron, iron fire etc. Alloy scrap iron, 103 alloy roll, spheroidal graphite roller, etc. Blast furnace material 104 dimensions should add more than lOmm X lOmm X lOmm X200mm X 200mm, 200mm, single weight less than 5kg processing block etc. 4.1.2.1.2