丙烯酸可再分散乳胶粉在刚性防水砂浆中应用-北京宝辰联合科技股份.pdfVIP

丙烯酸可再分散乳胶粉在刚性防水砂浆中应用 * 王辉 王霞 孙冬娟 （北京宝辰联合科技股份有限公司 北京 102200） 摘要：从力学性能、柔韧性、抗渗性、吸水率等角度研究了丙烯酸可再分散乳胶粉在刚性 防水砂浆中的应用，同时对EVA可再分散乳胶粉与丙烯酸可再分散乳胶粉在防水砂浆中性 能进行了对比，研究结果表明，当丙烯酸乳胶粉掺量超过2%时，48h吸水率小于6%；随 着乳胶粉掺量的增加，砂浆的本体抗渗能力提高，吸水率下降；当丙烯酸乳胶粉掺量达到 3%时，刚性防水砂浆压折比小于3。丙烯酸胶粉较EVA胶粉有更高柔韧性和较小的吸水率。 关键词：丙烯酸可再分散乳胶粉 防水砂浆 吸水率 抗渗性 Applicationofacrylicredispersiblepolymer powderinwaterproofing mortar Wanghui Wangxia Songdongjuan BossonChemicalCo.,Ltd.Beijing102200 Abstract: The effect of arylic redispersible polymer powder on waterproofing mortar was evaluated from mechanical properties, flexibility, impermeability, water absorption. The performance of EVA redispersible polymer powder in waterproofing mortar was also compared. The results showed the water absorption ratio was below 6% when the content of arylate redispersible polymer powder exceeded 2%; and the performance of impermeability and the water absorption was improved with the higher content of acylate redispersible polymer powder. The compressive/flexural strength was below 3.0 while the content of arylate redispersible polymer powder exceeded 3%. The mortar with arylate redispersible polymer powder than the mortar with EVA redispersible polymer powder showed excellent impermeability, lower water absorptionandbetterflexibility. KeyWords: acrylateredispersible polymerpowder,waterproofingmortar,impermeability 1 前言 刚性防水砂浆具有与基层和后继工序中材料相容性好的“双亲”的特性，可喷、可刷、 可抹，施工非常简便，对于活动性不是很大的基层，如隧道、地下室等，刚性防水砂浆非 常适用，在边角和活动性较大的部位可以配合柔性防水砂浆使用，以获得最优整体防水效 [1] 果 。只要配合比、施工方法适当，一般来说水泥基材料的抗渗性能非常优异，完全可以 满足防水要求，抗渗等级达到P12 非常容易，实际工程中水压一般很少超过0.3MPa，实际 工程中经常出现配制P12抗渗等级防水砂浆出现大面积渗水、漏水现象，不能满足抗渗防 [2] 水要求 。这是由于普通防水砂浆柔韧性不够，极易开裂，另外防水砂浆层厚度较小，由 于水泥基材料毛细孔吸水作用，使得防水砂浆吸水性太强，不能起到很好防水防潮作用。 * 作者简介：王辉，男，1981.1，宝辰联合上海运营中心主任，北京昌平区邓庄西，102200，电话：01080106229， E-mail：wanghui@ 因此，提高柔韧性和