研究 分析 实验 低温烧结NiCuZn 铁氧体的软磁特性 廖 杨 韩志全 任仕晶 中国西南应用磁学研究所 四川绵阳 621000 摘 要 用溶胶-凝胶法制备了NiCuZn 铁氧体 给出了Ni Zn Cu Fe O 的磁导率频谱曲线及 f 0.75 x x 0.25 2 4 i r M H T 随Zn 含量x 的变化 获得了在860~875 的烧结温度下 100kHz 下 起始磁导率 = 610~300 比 s c C i 损耗因子tan / = 1.1~4.6 10 6 和在880 下烧结 1000 的良好性能 i i 关键词 NiCuZn 铁氧体 低温烧结 溶胶-凝胶法 磁导率 中图分类号 TM277 文献标识码 A 文章编号 1001-3830(2004)05-0028-02 Soft Magnetic Properties of Low Temperature Sintered NiCuZn Ferrite From Powder Prepared by Sol-Gel Method LIAO Yang, HAN Zhi-quan, REN Shi-jing Southwest Institute of Applied Magnetics , Mianyang, 621000, China Abstract: The fine powder of NiCuZn ferrites was prepared by sol-gel method. The complex permeability spectra are shown for sintered Ni Zn Cu Fe O specimens with various Zn content x . The electromagnetic 0.75 x x 0.25 2 4 properties including initial permeability , cut-off frequency f , loss factor tan / , Curie temperature T , saturation i r i C magnetization M and coercive force H are given and discussed for these sintered Ni Zn Cu Fe O specimens. s c 0.75 x x 0.25 2 4 The samples exhibit i1000 at sintering temperature 880 , and i of 610 300