论混凝土裂缝原因-预防和处理.docVIP

论混凝土裂缝原因\预防和处理 　　摘要：钢筋混凝土裂缝的控制问题是建筑工程中很重要的问题之一，特别是随着泵送商品混凝土获得广泛应用之后，混凝土均质性有了很大改善的同时，裂缝控制技术难度大大增加了，本文是在大量建设实践和现场实验研究基础上，概述了变形作用引起裂缝的原因，约束变形特征，抗与放的设计准则以及最大裂缝宽度限值及预防进行了阐述。 关键词: 裂缝；分析；控制；水泥混凝土；钢筋混凝土 Abstract: reinforced concrete crack control problem is one of the important problems in the construction engineering, especially with the wide application of pumping concrete products obtained after concrete homogeneity has improved a lot at the same time, crack control technology has greatly increased the difficulty, this article is based on a large number of construction practices and field experimental research, summarizes the deformation effect, the causes of cracks constraint deformation characteristics, and put the design criterion of resistance and the maximum value of crack width and prevention are expounded. Key words: cracks; Analysis; Control; Cement concrete; The reinforced concrete 中图分类号：TU71文献标识码：A文章编号：2095-2104(2013) 钢筋混凝土常见裂缝原因分析 （一）混凝土裂缝的分类 混凝土裂缝是混凝土的一种常见病和多发病。病情绝大多数发生于施工阶段，其原因复杂多变，一般可分为微观裂缝和宏观裂缝两大类： 微观裂缝是指肉眼看不到的、砼内部固有的一种裂缝，它是不连贯的。宽度一般在0.05mm以下，这种砼本身固有的微观裂缝，荷载不超过设计规定的条件下，一般视为无害。 宏观裂缝宽度在0.05mm以上，并且认为宽度小于0.2~0.3mm的裂缝是无害的，但是这里必须有个前提，即裂缝不再扩展，为最终宽度。 （二）混凝土裂缝的成因 1、使用原因(外界因素) 构筑物基础不均匀沉降，产生沉降裂缝；使用荷载超负；野蛮装修，随意拆除承重墙或凿洞等，引起裂缝；周围环境影响，酸、碱、盐等对构筑物的侵蚀，引起裂缝；意外事件，火灾、轻度地震等引起构筑物的裂缝。 2、施工工艺原因 施工工艺涉及的面很广，一般常涉及到的有，一是水分蒸发、水泥结块的混凝土干缩通常是导致混凝土裂缝的重要原因之一。二是混凝土－种人造混合材料，其质量好坏的一个重要标志是成型后混凝土的均匀性和密实程度。因此混凝土的搅拌、运输、浇捣、振实各道工序中的任何缺陷和疏漏，都可能是裂缝产生的直接或间接原因。 3、荷载与外荷载的原因 由各类变形荷载，包括温度变形（水泥的水化热、气温变化、环境生产热），收缩变形（塑性收缩、干燥收缩、碳化收缩）及地基不均匀沉降（膨胀）变形，由于这些变形受到约束引起的应力超过混凝土的抗拉强度导致裂缝。下面逐一进行分析： （1）温度裂缝：温度裂缝多发生在大体积混凝土表面或温差变化较大地区的混凝土结构中。温度裂缝的走向通常无一定规律，大面积结构裂缝常纵横交错；梁板类长度尺寸较大的结构，裂缝多平行于短边；深入和贯穿性的温度裂缝一般与短边方向平行或接近平行，裂缝沿着长边分段出现，中间较密。 （2）干燥收缩裂缝：混凝土在空气中结硬时，体积会逐渐减小，即干缩；干缩裂缝的产生主要是由于混凝土内外水分蒸发程度不同及胶质体的胶凝等作用而导致变形不同所产生的结果。 （3）塑性收缩裂缝：指混凝土在凝结之前，表面因失水较快而产生的收缩。一般在干热或大风天气出现，主要原因是混凝土在终凝前几乎没有强度或强度很小，或者混凝土刚刚终凝而强度很小时，受高温或较大风力的影响，混凝土表面失水过快，造成毛细管中产生较大的负压而使混凝土体积急剧收缩，而此时混凝土的强度又无法抵抗其本身收