Minas Rio 赤铁精粉球团制备特性研究 ·1 · Minas Rio 赤铁精粉球团制备特性研究 朱德庆 师本敬 潘 建 钟 洋 （中南大学资源加工与生物工程学院，湖南长沙 410083 ） 摘 要 针对赤铁精粉成球性较差、焙烧温度高，导致在链箅机—回转窑球团原料中配比低的问题，对赤铁精粉配 加磁铁精矿及采用高压辊磨预处理造球原料的方法改善 Minas Rio 赤铁精粉的成球性及焙烧性能进行了研究。结果 : 表明: Minas Rio 赤铁精粉的成球性及焙烧性能相对磁铁精矿较差，膨润土用量大；按 6 4 的比例与不同种类的国 内磁铁精矿混合经高压辊磨处理后造球，膨润土添加量由 1.5%以上最低可降至 0.6% ，球团焙烧温度可降低 50~100℃，生球和焙烧球团强度均可满足生产要求。 关键词 赤铁精粉，球团特性，磁铁精矿，高压辊磨 Studies on the Pelletization of Minas Rio Hematite Concentrates Zhu Deqing, Shi Benjing, Pan Jian , Zhong Yang (School of Minerals Processing and Bioengineering, Central South University, Changsha 410083,China) Abstract Considering its lower ball-ability and higher firing temperature required during pelletizing, hematite concentrates ratio in pellet feed is restricted in rotary kiln process. Serials experimental studies on Minas Rio hematite concentrates pelletizing performance were conducted through varying Minas Rio blending ratio in hematite - magnetite concentrates mix and pretreating of the materials by high pressure roller (HPGR). The results show that the ball-ability index and firing performance of Minas Rio hematite concentrates are inferior to domestic magnetite concentrates. Without pretreatment of the pellet feeds higher bentonite dosage is required and lower strength of fired pellets is expected although at higher firing temperature. In contrast, after pretreatment by HPGR, the pellet feeds consisting of 40% domestic magnetite concentrates and 60% Minas Rio hematite concentrates r