Ta10W压缩力学性能实验研讨.pdf

Ta-10W 12 1 2 2 1. 610031; 2. 621900 MTS SHPB Ta-10W -1 -1 700s 3100s Ta-10W 930MPa1GPa Experimental Research on Mechanical Property of Ta-10W 1,2 1 2 2 ZHONG Wei-zhou , SONG Shun-cheng , XIE Ruo-ze , HUANG Xi-cheng (1Department of Applied Mechanics and Engineering, Southwest Jiaotong University, Chengdu 610031, China 2 Institute of Systems Engineering, China Academy of Engineering Physics, Mianyang 621900, China) Abstract: Quasi-static and dynamic compression experiments of unannealed Ta-10W alloy specimen are implemented by MTS and split hopkinson pressure bar equipments. Quasi-static compression yield strength is gained . Curves of stress vs strain and dynamic compression yield strength are obtained when strain rate -1 -1 is from 700s to 3100s . Based on the experiment results, Unannealed Ta-10W is preferably flexile alloy. There is no crack occured on the surfaces of specimens in the experiments. The quasi-static and dynamic compression strength of unannealed Ta-10W alloy is quite large. Quasi-static compression yield strength is about 930MPa. And the dynamic compression yield strength is over 1GPa. Dynamic compression yield strength of Ta-10W is dependent on strain rate. It becomes a little greater when strain rate increases in the dynamic experiments. Key words: tantalum tungsten alloy; mechanical property; strain rate; compressione experiment / [1-2]