巨磁阻抗现象的研究 要：本文研究了在纵向驱动下，Fe基纳米晶带出现超巨磁阻抗现象的条件及出现此现象的原因。所谓超巨磁阻抗现象，即在纵向驱动下，Fe基纳米晶带的阻抗曲线在某一个很小磁场范围内变化非常灵敏，此时阻抗值和巨磁阻抗效应均很大，阻抗最大值可达Z=73187.5 KΩ，巨磁阻抗效应最大值可达(Z- Z0)/ Z0=ΔZ/ Z0 =13758.036%。其原因之一可能为当样品本身的固有频率和由线圈和晶带共同组成的等效元件的LC共振频率一致时，出现双共振现象。 关键词： 双共振 固有频率 LC共振 纵向驱动巨磁阻抗效应 Fe基纳米晶带 Studies Of The Phenomenon Of extra Giant Magneto-impedance Wang Xiaoyan1 1（Jiangshan middle school of Ningbo, NingboZheJiang 315191） Abstract: The condition and causation of the phenomenon of extra Giant Magneto-impedance on t he longitudinal driven in Fe-based nanocrystalline ribbon was investigated .It is the phenomenon of the extra Giant Magneto-impedance that the impedance curve of Fe-based nanocrystalline ribbon has changed very quickly in the small range of the magnetic field. Also the impedance and Giant Magneto-impedance effect are very great. The max impedance can reach Z=73187.5 KΩ, and the max Giant Magneto-impedance effect also can reach (Z- Z0)/ Z0=ΔZ/ Z0 =13758.036%. One of the reasons of this phenomenon maybe is double resonance. When the inherent frequency of the sample is according with the frequency of the LC resonance of the equivalent component which is made of coil and nanocrystalline ribbon, the double resonance is happened.. Keywords: Double resonance; Inherent frequency; LC resonance; Longitudinal driven GMI effect; Fe-based nanocrystalline ribbon; 1 引言 自从1992年Mohri等人首先在Co基非晶丝中发现了巨磁阻抗效应[1]以来，后来，人们很快在Fe基非晶丝、薄带中也发现了巨磁阻抗效应[6]。一般认为，具有优异软磁特性的材料是获得GMI效应的前提[8，9]。近年来有学者研究过纵向驱动巨磁阻抗效应，即用纳米晶带和线圈组成一个等效的阻抗元件，线圈通过的交变电流对样品产生一个纵向的驱动磁场，线圈二端的磁致阻抗变化最高达1600%。这种驱动方式的交变电流并不直接通过样品，可避免样品引线的接触以及样品本身的焦耳热损耗。同时纵向驱动巨磁阻抗效应要远远大于横向驱动巨磁阻抗效应[3，4]。 本文着重研究了Fe73.5Cu1Nb3Si13.5B9纳米晶带的纵向驱动巨磁阻抗效应，发现纳米晶带的超巨磁阻抗现象，即阻抗曲线在一个很小的磁场范围内变化非常灵敏，阻抗峰很尖很锐，同时阻抗值和巨磁阻抗效应也非常大。本文对巨磁阻抗曲线的形状和大小、阻抗效应的大小与线圈的规格和驱动电流的频率的关系进行了讨论，初步分析了出现超巨磁阻抗现象的原因。有关超巨磁阻抗现象还未有文献见报 道。 2 实验 本实验所采用的晶带是用单辊快淬法喷制Fe73.5Cu1Nb3Si13.5B9非晶薄带，然后在氮气保护下，温度在540℃，退火40分钟而制成。晶带为Fe73.5Cu1Nb3Si13.5B9粗晶带