以水热法合成BCTZBaxCaxTiyZryO3奈米粉末之研究-成功大学.PDFVIP

第二屆資源工程研討會論文集 以水熱法合成BCTZ(Ba Ca Ti Zr O )奈米粉末之研究 1-x x 1-y y 3 1 2 3 郭政男 、向性一 、宋志剛 摘要 本研究以 BaCl2 、CaCl2 、TiCl4 、ZrOCl2 為前驅物，利用水熱法合成 BCTZ 粉末。固定 A/B ratio ((Ba+Ca)/(Ti+Zr)) 、NaOH 過量、反應溫度、持溫時間，來探討水熱參數 (起始四氯化鈦濃度的不同、對粉體性) 質的影響。合成的粉體將以 X 光繞射分析儀、場發射掃瞄式電子顯微鏡、鑑定其結晶結構、顆粒大小、形態和 其純度之不同。發現當反應條件為 A/B 比2.0 、Ti起始濃度 0.4M 、NaOH 過量 2M 、反應溫度200° 、持溫時間 2h可穫得大小約為 30-40nm 之分散且成份較均勻的奈米粉體。 關鍵詞： 鈦酸鋇、水熱法。 ABSTRACT In this study, BCTZ powders were synthesized using hydrothermal method from BaCl , CaCl , TiCl , ZrOCl .The 2 2 4 2 influences of Ti initial concentration on the properties of BCTZ powders were investigated. The crystal structures, particle sizes and morphologies of the synthesized powders were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM)). The BCTZ powder with the particle sizes of 30-40nm was obtained when Ba/Ti ratio was 2.0, Ti initial concentration was 0.4M, NaOH excess was 2M and reaction temperature was 200℃ for 2h 。 Keywords: BaTiO3 、Electrical ceramic 、Hydrothermal method 1國立成功大學資源工程學系碩士班研究生 2國立成功大學資源工程學系副教授 3 義守大學材料科學工程學系副教授 432 第二屆資源工程研討會論文集 從加熱包中取出，放置於空氣中使之自然冷卻至室 一、前言 溫，接著將生成之溶液及沈澱物自鐵氟龍內襯中倒 出，並以去離子水水洗數次，清除其他雜質後，以抽 由於 3C 產業蓬勃發展，電子元件的市場需求也