压敏胶技术原理--简化中文版.ppt

压敏胶技术原理 压敏胶的定义Definition of PSA 拥有持久的高粘性Aggressively and permanently tacky 应用时只需用手或手指施压Adheres with finger or hand pressure 不需通过水, 溶剂或加热活化Requires no activation by water, solvent or heat 有牢靠的粘接力Exerts a strong holding force 有足够的内聚力和弹性Has sufficient cohesiveness and elasticity 压敏胶的优点 PSA Advantages Ready to use, no mixing or brushing is required 迅速施胶，无需混合或涂刷。 Consistent amount of adhesive 均匀的胶量。 Less messy than super glue and contact cement 比胶水干净。 Can be die cut into specific shapes 可模切成特殊形状。 Stays viscoelastic which eliminates brittle fracture possible with epoxies, hot melts and cyanoacrylates 具有粘弹性，消除脆性。 Less odor during use 使用时低气味。 初 粘 力 与 终 粘 力Initial and Ultimate Adhesion 粘接力和内聚力 粘接力Adhesion  存在两种不同表面之间的吸引力 内聚力Cohesion 材料自身分子之间的吸引力 粘性和粘弹性Viscosity and Visco-elasticity 软 性 与 硬 性 压 敏 胶 Soft and Firm Adhesives 剥离强度与剪切强度的测试Peel vs Shear Test 动 态 剥 离 强 度(Dynamic Peel Adhesion) ---- 反映粘性, 操作方便 Force required to peel standard area of tape from a test panel at specific angle and constant speed Variables 变量 Speed 剥离速度 Test Panel Material and Surface Conditions Temperature 静 态 剪 切 强 度(Static Shear Strength) ----- 反映内聚力, 持粘性 Time required to shear a defined area of tape from a test panel at constant load Variables变量 Load 载荷 Test Panel Material and Surface Conditions 试验板材及表面状况 Temperature 温度 压敏胶的种类Pressure Sensitive Adhesive 橡胶类 Rubber Adhesives 天然胶 Natural Rubber 合成橡胶 Synthetic Rubber 丙烯酸类 Acrylic Adhesives 纯丙烯酸类 Standard Acrylic 改良丙烯酸类 Modified Acrylic 硅胶类Silicone Elastomer Adhesives 胶粘剂类别 压敏胶的选择 底材-----粘接难易程度（高/低表面能） 应用环境和使用寿命-----室内/户外、紫外线、耐温性 最终产品-----暂时/永久粘接 、透明/颜色 工艺流程-----模切（离型纸）、基材、操作速度、环境清洁 成本-----厚度、面积等 粘接失败的原因?What Causes Bond Failure? 压敏胶与底材不匹配 Adhesive-Substrate Incompatibilty 表面平整度 Surface Texture 表面污染 Surface Contamination 脱模剂 Mold Relea