生土墙体材料的试验研究与分析推荐.docVIP

PAGE 摘 要 生土建筑在我国有着长久的建造历史，其分布和应用范围也相当广泛。在社会普遍重视低碳生活，循环经济，可持续发展的新世纪，生土建筑材料有理由再次引人关注、探索和再研究。但是，传统的生土材料强度较低、耐水性差，严重地限制了生土材料的应用。加强对生土材料的改性研究，改善其性能，对扩大应用范围、提高使用效率、降低使用成本等具有重要意义。 本文利用脱硫石膏、矿渣和石灰等掺合料改性生土材料，分别采用压制成型和浇筑成型两种成型方式，以提高强度为主要目标对生土材料进行正交试验。结果表明，压制成型时，外掺掺合料的最佳配比为：矿渣 21%，脱硫石膏 3.5%，石灰 8.8%；浇注成型时，外掺掺合料的最佳配比为：矿渣 7%，脱硫石膏 14.5%，石灰 11.8%。改性后的生土材料，抗压强度可以提高 3-6倍，其中，压制成型掺加的改性材料较少，而且强度明显优于浇筑成型。 试验还进一步研究了各试验因素对生土材料性能的影响。矿渣、脱硫石膏、石灰等的掺入，大大改善了生土材料的耐水性。 关键词：生土材料；改性；强度；耐水性 Abstract The raw soil construction has the long time construction history in our country, its distribution and application scope are also quite widespread. Universal recognition the low-carbon life in the society, the circulation economy, the health sustainable development new century, raw soil construction all sorts of superiority also again studies on attracting attention even more with the exploration. However, the traditional raw soil material has fatal flaws, such as poor compressive strength and low water resistance and volume stability, which restricted its application seriously. Therefore, strengthening its modified research to improve its performance have vital practical significance in expanding the application scope, improving service efficiency and reducing the cost etc. The research is conducted to utilize desulfurization gypsum, slag and lime modified raw soil material. The orthogonal experiment with strength for the main target dose preliminary exploration for the best mixing of modified soil; which mould through compressing and casting. The test result is as follows respectively: Optimum ratio by compression: slag 21%, desulfurization gypsum3.5%, lime 8.8%; Optimum ratio by casting: slag7%, desulfurization gypsum 14.5%, lime11.8%. The strength of modified materials can be improved by 3 to 6 times. The strength of mode with less doped modified material through compressing is obviously better than the one through casting. The research has further discussed that the influence of modifi