fegaer磁致伸缩合金组织结构及性能word格式论文.docx

magnetostrictivecoefficientafterquenchingtreatmentissignificantlyincrease,whichimproveto32ppm~57ppm.Thegrainshapeandorientationaredifferent,afterdifferentheattreatmentconditions.Thecrystalofhotrollingstatealloybeforceheattreatmentislong cylindricalinshapeandgrowthdirectionhasacertaindirection.Crystalbecomeisometriccrystalafterheattreatment.Byenergyspectrumanalysis,thewhitereticulationwithinthecrystalboundary isrichinEr,which isthoughtisphaseofrich Erinprimary.Key Words：Fe-Gaalloys；Er；Magnetostrictive；MicrostructureIII目录摘要.........................................................................................................................IAbstract..........................................................................................................................II引言........................................................................................................................11 文献综述....................................................................................................................21.1 磁致伸缩简介..................................................................................................21.1.1 磁致伸缩效应........................................................................................21.1.2 磁致伸缩的微观理论............................................................................21.1.3 磁致伸缩的唯象理论............................................................................31.2 磁致伸缩材料概况..........................................................................................41.2.1 磁致伸缩材料的应用............................................................................41.2.2 磁致伸缩材料的发展历程....................................................................61.3 Fe-Ga 合金的研究概况和进展61.3.1 Fe-Ga合金磁致伸缩应变的机理61.3.2 Fe-Ga合金的研究进展81.4 选题背景及研究内容....................................................................................131.4.1 选题背景..............................................................................................131.4.2最近Fe-Ga-RE合金研究的情