毕业设计（论文）多孔二氧化钛光催化性能评价条件研究.docVIP

毕业设计（论文）--多孔二氧化钛光催化性能评价条件研究 攀枝花学院本科毕业设计论文 多孔二氧化钛光催化性能评价条件研究 院 系 生物与化学工程学院 专 业 化学工程与工艺 学生姓名 陈俊恩 学 号 4 指导教师 田从学 副教授 com 摘要 TiO2是一种能够净化环境的绿色功能材料它不仅具有氧化能力强无选择性能耗低无二次污染降解完全等优点而且还具有价廉无毒可长期使用等特点所以它成为近年来光催化技术研究的热点并且广泛用于催化剂颜料等领域简称MB考察了不同光催化条件下二氧化钛对亚甲基蓝降解率的影响吸收波长666nm亚甲基蓝溶液pH50甲基蓝溶液浓度催化剂用量gL亚甲基蓝 多孔二氧化钛 催化剂用量pH值光催化 ABSTRACT Titania is a green functional materials capable of decontaminating the environment due to its merits of strong oxidizing ability non-selectivity low energy consumption no secondary pollution degradation completely etc as well as cheap non-toxic long-term photostability in recent yearsit Therefore in recent years it has become research focus of photocatalytic technology and it is widely used in catalyst pigmentsand and other fields In this paper metatitanic acid used as raw material photocatalytic experiments carried out in different conditions to investgate the effects of on porous titania structure and photocatalytic performances The as-prepared powders were characterized by XRD FT-IR paritcle size distribution test specific surface area measurement etc 后面自己修改翻译The photocatalytic property of the prepared porous titanium was evaluated by a model of degrading MB And the optimal experimental conditions are absorbed wave length of 666nm pH 50 and catalyst dosage of 10 gL Key words Methylene blueporous titania catalyst dosage pH value photocatalysis 目 录 摘要 I ABSTRACT II 1绪论 1 11课题研究背景 1 12课题研究意义 1 13光催化材料的应用现状 2 14光催化原理 4 15课题研究思路 7 2实验部分 7 21实验药品与试验仪器 7 com品 7 com备仪器及装置图 8 22实验步骤 9 23样品的分析检测 10 com析 10 com谱分析 11 com XRD衍射分析 11 com 扫描电镜测试SEM 12 com积测定 BET 12 3结果分析与讨论 13 31吸收波长的影响 13 32 MB浓度的影响 13 33 初始浓度的影响 14 34 pH的影响 15 35 TiO2用量的影响 16 36 时间对MB降解率的影响 17 37 煅烧温度对降解率的影响 18 38表征测试分析 19 com 粒度分析 19 com 红外光谱分析 20 com XRD衍射分析 21 com 扫描电镜分析 21 com 比表面积分析 22 4 结论与展望 24 41结论 24 42展望 24 参考文献 27 附录 29 致谢 31 1绪论 11课题研究背景 进入21世纪以来人类社会工业文明迅猛发展全球工业化进程不断加剧与此引发的环境问题也不断加剧人类的生产活动和消费活动等对环境的污染日益严重城市