预变形法制备7075铝合金坯料半固态微观组织演变规律及形成机制-semi-solid microstructure evolution and formation mechanism of 7075 aluminum alloy billet prepared by pre-deformation method.docxVIP

SIMArouteandFSP(frictionstirprocessing)route,theresultsareasfollow:1)ahighdegreeofrecrystallizationmicrostructurepreparedbyFSProutecanobtainfineandroundsolidgrainsinshortertimeduringsemisolidprocess;2)ThesemisolidstructureobtainedbyRAProuteisfinerandrounderincomparisonwithSIMAroute,owingtoobtainingmorestoredenergyafterpredeformationofRAProute,thus,mostofmicrostructurefirstlyoccurrecrystallization;3)Coarseningofgrainsandrecrystallizationofalloytarecloselyrelated,themorerecrystallizationgrainsoccurduringremelting,themoregrainsgrowbyroleOstwaldripeningmechanism;4)thequalityofsemisolidbilletandrecrystallizationofsolidbilletarecloselyrelated,thedegreeofrecrystallizationishigher,thesolidgrainsofsemisolidbilletarefinerandronder.Keywords:7075aluminumalloy,extrusiondeformation,recrystallization，Semi-solid,Microstructureevolution目录中文摘要..........................................................................................................................................I英文摘要........................................................................................................................................II1绪论......................................................................................................................................11.1引言...........................................................................................................................................11.2半固态坯料的制备...................................................................................................................21.2.1应变诱导熔化激活法........................................................................................................21.2.2再结晶重熔法....................................................................................................................41.2.3机械搅拌法........................................................................................................................61.2.4电磁搅拌法....................................................................................