配合比对海工混凝土耐久性影响试验研究 　　[摘 要] 相当数量的海工混凝土结构因为耐久性不足而达不到预定服役年限，而氯离子是“罪魁祸首”。目前，矿物掺加料对于提高混凝土的抗渗性，尤其是提高抗氯离子扩散性能有着显著效果。文章结合具体实验，研究了矿物掺合料对混凝土强度的影响和氯离子扩散系数随矿物掺合料掺量的变化规律，并探讨矿物掺合料的最优掺量问题，为海工混凝土配合比设计提供了一些建议。 　　[关键词] 海工混凝土 矿物掺合料 氯离子扩散系数 配合比设计 　　[Abstract] A considerable number of marine concrete structures because of insufficient durability and reach the scheduled service time, while the chloride ion is the culprit. At present, the mineral admixture materials to improve the impermeability of concrete, in particular, is to improve the resistance to chloride ion diffusion properties have a significant effect. Based on specific experiments studied the influence of mineral admixtures on the strength of concrete and chloride ion diffusion coefficient variation with the mineral admixture content, and to explore the optimal dosage of mineral admixtures for marine concrete with than the design of a number of recommendations. 　　[Key words] marine concrete, mineral admixture, the chloride ion diffusion coefficient, mix design中图分类号：TU377 文献标识码： A 文章编号： 　　 　　1 概述 　　矿物掺合料的应用越来越广泛，被称为混凝土的“第四组分”[1]， 而目前的配合比设计也主要集中在矿物掺加料上[2-4]。但是矿物掺合料的掺量是不是存在一个最优掺量，结果不得而知。另外，矿物掺合料对混凝土强度和氯离子扩散系数有怎样的影响，也是要研究的问题。 　　2 试验 　　2.1试验原材料 　　2.1.1 水泥 　　试验所用的水泥为烟台三菱水泥有限公司生产的42.5R级普通硅酸盐水泥。水泥的具体物理化学性能指标和强度指标分别见表2.1、2.2。 　　表2.1 水泥的物理化学指标 　　 　　 　　表2.2 水泥的强度指标 　　 　　 　　河砂，表观密度为2200 Kg/m3。砂的细度模数为3.09，属于中粗砂，砂的颗粒级配符合JGJ 53-92的要求。 　　2.1.3 石子 　　采用5-20mm的连续级配。堆积密度为1667Kg/m3，比重为2.61。实验前将石子冲洗干净，??干。 　　2.1.4 水 　　采用自来水。 　　2.1.5 减水剂 　　YJ2-1型早强减水剂，灰色固体粉末状，减水率达12%以上。 　　2.1.6 矿物掺加料 　　试验使用的粉煤灰（Ⅲ级）为威海热电厂生产；矿渣为S95级，济南钢厂生产。粉煤灰和矿渣的具体性能指标见表2.3和表2.4所示。 　　表2.3 粉煤灰性能指标（Ⅲ级） 　　 　　表2.4 矿渣性能指标（S95级） 　　 　　 　　2.2试验配比设计 　　我国混凝土结构耐久性设计与施工指南中提到，粉煤灰和矿渣对混凝土耐久性能和强度的贡献受水胶比的影响较大，尤其是粉煤灰更为敏感。只有在低水胶比下（小于0.4或0.42），粉煤灰和矿渣的作用才能得以充分发挥而不是相反。 　　在参阅相关文献[5,6]后，决定拟研究试验的水胶比分别为0.35和0.4，实验中固定砂率38%，凝胶材料用量固定为460kg/m3,粉煤灰掺量分别为25%、30%和35%，矿渣掺量为50%、60%和70%。混凝土中掺用粉煤灰和矿渣都采用等量取代法。具体实验配合比见表2.5。 　　表2.5 试验配合比方案 　　 　　 　　3 配合比对混凝土抗压性能的研究 　　将试验试件所测的强度与设计强度做比