无铅易切削石墨黄铜的制备及性能分析-preparation and performance analysis of lead-free free-cutting graphite brass.docxVIP

 PAGE 6 ABSTRACT region in brass matrix that cause the notch effect by cutting off the continuity of the matrix. The existence of these regions make cutting process to be easier. In addition, graphite is easier to achieve a smooth surface as a good lubricant due to forming a layer of graphene in tool and metal surface. The corrosion resistance property of graphite brasses are increased with the cast iron content increased from 1% to 5%, but decreased with the content of 7% cast iron. The corrosion resistance property of graphite-brass is a result of joint action by microstructure, the component and the distribution of graphite particles. The tensile strength, elongation, Vickershardness and dezincification depth of graphite-brass added with 5% eutectic cast iron are 502 MPa, 22.6%, 148.9 HV and 144.2 μm, respectively. The chips are desired. The samples surface smoothness is relatively high after machining. The mechanical properties, cutting performance and corrosion performance of the graphite-brass are the best, that are far superior to bare brass. So it is feasible that the graphite-brass replaces leaded brass. Key Word: graphite-brass, graphitization of cementite, microstructure, cutting performance, corrosion resistance property 目 录 目 录  HYPERLINK \l _bookmark0 第一章 绪论 ···················································································1  HYPERLINK \l _bookmark1 1.1 研究背景 1  HYPERLINK \l _bookmark2 1.2 黄铜的切削性能 2  HYPERLINK \l _bookmark3 1.2.1 评定切削性能的主要指标 2  HYPERLINK \l _bookmark4 1.2.2 影响切削性能的主要因素 2  HYPERLINK \l _bookmark5 1.2.3 铅在黄铜中的作用机理 3  HYPERLINK \l _bookmark6 1.3 无铅易切削黄铜的研究进展 4  HYPERLINK \l _bookmark7 1.3.1 以铋代铅的易切削黄铜 4  HYPERLINK \l _bookmark8 1.3.2 以锑代铅的易切削黄铜 5  HYPERLINK \l _bookmark9 1.3.3 以镁代铅的易切削黄铜 6  HYPERLINK \l _bookmark10 1.3.4 以硅代铅的易切削黄铜 6  HYPERLINK \l _bookmark11 1.3.5 以石墨代铅的易切削黄铜 7  HYPERLINK \l _bookmark12 1.4 无铅黄铜的腐蚀性能 10  HYPERLINK \l _bookmark13 1.4.1 黄铜脱锌腐蚀