铁矿粉流态化还原过程中的粘结失流分析-analysis of bond loss during fluidization reduction of iron ore powder.docxVIP

thecarbonmonoxideasthereductiongas.Thereweretwodifferenttypesofdefluidizationphenomenonbycontrastthesurfacemorphologyofspecimensbeforeandafterdefluidizationundervariousoperatingconditions.Oneisduetowhiskerconnectedtoeachotherwhenthereductiongasiscarbonmonoxide,theotheriscausedbysofteningormeltingofironunderhightemperaturewhenthereductiongasishydrogen.Keywords:non-blastfurnaceiron-making;fluidizedbed;stickinganddefluidization;whisker目录中文摘要..........................................................................................................................................I英文摘要........................................................................................................................................II1绪论..............................................................................................................................................11.1引言........................................................................................................................................11.2流态化技术在炼铁方面的应用............................................................................................11.3流态化还原技术的应用前景分析........................................................................................61.4铁矿粉流态化还原过程中的粘结失流研究现状................................................................81.4.1粘结失流的发生机理..................................................................................................81.4.2影响粘结失流的因素..................................................................................................91.4.3抑制粘结失流的措施................................................................................................111.5研究背景和内容..................................................................................................................121.5.1研究背景....................................................................................................................121.5.2研究内容......................................................................................